Scanning Electron Microscope

74 cases · 354 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage clear all

Scanning Electron Microscope — sub-branches

Electrolytic Etch Micrography by SEM 5Fractography by SEM 166Kalling Etched Micrography by SEM 2Micrography by SEM 50Nital Etched Micrography by SEM 39Surface Aspect by SEM 92

Results

SortNewestOldestTitle A-ZTitle Z-A
The same fracture appearance of the previous figure, looking at a higher magnification by scanning electron microscopy. The fracture is clean, flat, starting in the right side of the figure, at the margem of the weld and propagating into the pipe thickness. The external side of the pipe is to the right side of the figure and the internal side of the pipe is to the left side of the figure.
154
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fracture
Aspect by scanning electron microscopy of the brittle fracture surface. in a low magnification view. The fracture presents smashed regions (conditions imposed after the fracture was opened) in the region where the chevron marks indicate it is the failure starting point.
26
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Brittle Fracture
Micrography, by scanning electron microscopy. The alloy is a precipitation hardened material, and the stains at the surface are associated to differential etching in second phases and inclusions.
35
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Micrography by SEMDf - Granular structure
Micrographic detail by scanning electron microscopy of the interface between the two thermal spray layers, the first one in stainless steel (bottom of the figure) and the second one, at the surface,in tungsten carbide (top of the figure). The composition of the first layer is similar to the base metal (lean duplex) and the composition of the second layer is WC in a Co matrix.
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Electrolytic Etch Micrography by SEMDf - Thermal Spray Layer
Micrography of the plate in a section, showing the alpha grains plus beta phase microstructure in the middle of the thickness. The sample was mechanically-electrolitically polished and etched with HF+HNO3+H2O solution.
27
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by SEMDf - Alpha and Beta
Micrography of the plate section, in the middle of the plate in a position where the projectile did not affect. Ferritic-pearlitic structure.
55
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by SEMDf - Ferrite and Pearlite
Micrography of the plate section, in the middle of the plate. Martensitic structure.
47
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Nital Etched Micrography by SEMDf - Martensite
The fracture surface of the casting cylinder presented, at the internal surface, interconnected graphite flakes and a corroded matrix.
73
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Close to the Internal Surface

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Fracture apperance by scanning electron microscopy of the region where the fatigue crack started, from the piping outside . The fracture is flat, presents some smashed regions close to the surface (to the right side) and there are some thin secondary cracks.
140
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Fracture detail by scanning electron microscopy of the region where the cracking started, from the piping outside . The fracture is flat and shows fatigue striation.
138
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture apperance by scanning electron microscopy in the center of the thickness where the crack propagated through wall. The fracture is flat and the striation is not so clear at this magnification.
133
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Fracture detail by scanning electron microscopy of the region cloin the center of the thockness. The fracture is flat and shows fatigue striation.
118
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Observing in higher magnification it is possible to see that the fracture presents a mixture of ductile and brittle micromechanisms. The intergranular mechanism indicates that the material is embrittled and the dimples indicate localized overloading conditions.
32
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Fracture
Detail of the ductile dimples and the brittle intergranular micromechanisms. This evidence (a mixture of mechanisms) suggests that the embrittlement is localized in some regions of the material.
34
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Fracture
Scanning electron microscope fractographic detail of the brittle intergranular micromechanism.
40
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Intergranular Fracture
Scanning electron microscope fractographic detail of the ductile dimples.
26
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Dimples
ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Micrographic detail, by scanning electron microscopy, of the precipitation hardened granular structure. The stains are preferential etch of second particles.
32
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Micrography by SEMDf - Aligned particles
Detail of the margin of the perforated hole in the impact position. It is interesting to observe extreme plastic deformation created by the perforation expulsing the material from the hole, in the direction of the impact.
28
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - Plastic Deformation
Detail of the plate surface showing striation as the finishing, deformed by the projectile effect in shearing the thickness.
24
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the plate surface showing striation as the finishing, deformed by the projectile effect in shearing the thickness.
24
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - At the Surface
High magnification detail of the plate surface showing the deformed striation.
21
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - At the Surface

+17 more from this case →

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Micrographic detail of the first thermal spray layer, in stainless steel with the same composition of the base metal (lean duplex).
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Electrolytic Etch Micrography by SEMDf - Thermal Spray Layer
Micrographic detail, by scanning electron microscopy, of the duplex, austenitic and ferritic, structure with sigma phase.
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Electrolytic Etch Micrography by SEMDf - Sigma
ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrographic detail by SEM, showing the beta phase EDS analysis was conducted in this microstructure and the results indicated 90.8%Ti + 6.8%Al + 2.4%V for the alpha phase (the dark grains as a matrix); and 84.7%Ti + 5.2%Al + 8.8%V + 1.2%Fe for the beta phase (light with aicular morphology inside the phase).
25
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by SEMDf - Alpha and Beta
Aspect of the surface of the plate by scanning electron microscopy, at the impact position, showing that the bullet was melted and deposited. The plate presented round cracks in the margin of the projectile impact position.
14
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Aspect of the surface of the plate, by scanning electron microscopy, in the center of the projectile impact position, showing the melted bullet covering the surface.
14
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Detailed aspect of the surface of the plate at the projectile impact position.
12
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Aspect of the surface of the plate, by scanning electron microscopy, out of the center of the projectile impact position, showing that the melted bullet covered a large part of the surface.
12
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film

+19 more from this case →

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Micrographic detail of the plate section, evidencing the non affected ferritic-pearlitic structure.
57
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by SEMDf - Ferrite and Pearlite
Detail of the margin of the perforated hole in the impact position. It is interesting to observe extreme plastic deformation created by the perforation expulsing the material from the hole, in the direction of the impact.
42
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - Plastic Deformation
Margin of the perforated hole showing regions of fracture and a smooth appearance in the hole surface (right side of the figure). This smooth aspect was generated by the film of melted material from the bullet.
44
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Ductile Fracture
The fracture created by the projectile impact is fully ductile. The material presented a sheared surface with elongated dimples.
45
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Dimples
Fractographic detail of the ductile fracture generated by the projectile impact. The material presented a sheared surface with elongated dimples.
41
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Dimples

+11 more from this case →

ML00142 — Impact of a .308 Winchester on AR500 PlateM - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Micrographic detail of the plate section presenting the martensitic microstructure.
43
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Nital Etched Micrography by SEMDf - Martensite
Microscopically aspect of the plate surface at the bullet impact, by scanning electron microscopy, presenting the foreign material from the bullet adhered at the surface.
34
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Low Mag
Microscopically aspect of the plate surface in the center of the bullet impact. The light and smooth surface is the melted bullet on the plate and the dark surface is the steel plate with oxides and very small surface cracks (10 microns length).
30
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Detailed aspect of the plate surface where there was the bullet impact, by scanning electron microscopy, showing that the bullet has melted and solidified on the surface. The EDS analysis showed Pb-Sb peaks.
32
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Aspect of the plate surface a little far from the region of bullet impact, by scanning electron microscopy, showing bullet melted islands on the surface. The EDS analysis showed Pb-Sb peaks.
25
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface

+1 more from this case →

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
The fracture surface of the casting cylinder presented, in the center of the thickness, cleavage facets and graphite decohesion that corresponds to a brittle fracture of the material.
61
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - In the Center of the Thickness
The fracture surface of the casting cylinder presented, close to the external surface, a more ductile aspect of the fracture.
58
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Close to the External Surface
Fractographic detail of the interconnected graphite flakes and corroded matrix.
50
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Corrosion
Fractographic detail of the graphite decohesion and cleavage facets in the center of the cast cylinder thickness.
47
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
Micrography of the longitudinal section of the cylinder, at the external diameter (right side of the figure), presenting smaller interdendritic graphite flakes in a ferritic-perlitic matrix. This surface is painted.
32
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by SEMDf - Graphite in Flakes