Scanning Electron Microscope

2 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Carburized Layer clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 6Surface Aspect by SEM 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Even in a sound tooth there are regions of pitting, and foreign incrustation, probably caused by metal removal and high contact spots.
53
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface Aspect by SEMDf - Pitting
Scanning electron fractography of a chromium plated pin, close to the pin surface where the fatigue cracking started, showing intergranular morphology typical of a hydrogen embrittlement effect. It occurred because the low alloy pin was carburized, quenched and tempered, with a too high hardness structure, before the electrolytic plating.
837
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture

More from these cases

ML00181 — Wear of a Carburized Hypoid GearM - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Aspect of the fractured tooth in a region presenting pitting, opening voids, and cracks.
51
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface Aspect by SEMDf - At the Surface
Aspect of the fractured tooth surface in a region presenting pitting, spalling and cracks.
42
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface Aspect by SEMDf - Spalling
Microscopic aspect of the cracks at the tooth surface. The cracks are flat and propagating longitudinally to the tooth (and secondary short transverse).
45
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface Aspect by SEMDf - Cracks
Microscopic aspect of the fracture, propagating by contact fatigue.
43
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Fractography by SEMDf - Fatigue Fracture
ML00081 — Hydrogen Cracking of a Chromium Plated Carburized PinM - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Scanning electron fractography showing that the fracture micromechanism is intergranular close to the surface of the pin, suggesting a hydrogen embrittlement effect at the carburized layer. The cracks were created during the electrolytic plating, and propagated later during service.
44
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - At the Surface
Scanning electron fractography of the pin in the fatigue subcritical crack growth, showing striation and regions of smashing .
40
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Fatigue Striation
Fractographic detail of the fatigue striation in the subcritical crack growth.
37
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Fatigue Striation
Fractography of the final fracture of the pin, presenting dimples (ductile fracture), after the nucleation and subcritical propagation of fatigue fracture.
36
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Dimples