Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Seamless Pipe Microstructure: Austenite clear all

Optical Microscope — sub-branches

Chromic Acid Electrolytic Etched 3Eletrolytically Etched Micrography by OM 6Micrography by OM 2Micrography by OM using A262 Method A 4Nital Etched Micrography by OM 15Oxalic Acid Electrolytic Etch 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe (seamless), that shows the through wall cracking, straigth and not associated to any welded region or microstructural problem.
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Through Wall Cracking
Micrography of the base metal presenting a banded microstructure in the longitudinal section of the pipe.
51
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a transverse section of the pipe, presenting the pitting corrosion. As polished.
310
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OMDf - Pitting

More from these cases

ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
72
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure.
68
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
67
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image. Some decarburization of the low alloy steel substrate is evident since the microstructure is slightly different a little far from the interface.
66
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
59
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+7 more from this case →

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Micrography of the pipe in a longitudinal section, close to the external surface, showing a pit (adjacent to the through wall cracking). The corrosion spt is not associated to any microstructural feature.
61
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Pitting
Micrography of a longitudinal section of the pipe presenting a granular austenitic structure, typical of a solid solution annealing condition. No carbide precipitation.
62
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Micrographic detail of a longitudinal section of the base metal presenting a quenched and tempered microstructure.
49
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the low temperature heat affected zone of the pipe. The intercritical temperature (IC) is evident in the decorated grain boundaries of the previous austenite.
42
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the fusion line close to the cap pass (CP). The weld metal (non etched) is in the left side.
43
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the heat affected zone, a little far from the fusion line, close to the base metal.
40
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the fusion line in the center of the thickness, where the heat affected zone was reheated by the subsequent passes.
34
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line

+8 more from this case →

ML00014 — Pitting Corrosion in 316SS PipeM - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Austenitic structure at the transverse section of the pipe, free from carbides.
277
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Austenitic structure, free from carbides, exactly in the region of the pitting, indicating that the corrosion is not associated to the material microstructure.
261
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite