Optical Microscope

9 cases · 49 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austenite Standard: ASTM Detail focus: Sampling and Analysis clear all

Optical Microscope — sub-branches

As polished micrography 4Eletrolytically Etched Micrography by OM 6Glyceregia Etched Micrography by OM 2Kalling Etched Micrography by OM 9Micrography by OM 3Micrography by OM using A262 Method A 15Nital Etched Micrography by OM 10

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
63
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
45
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography close to the external surface of a new tube, sound.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
Micrography of the base metal presenting a banded microstructure in the longitudinal section of the pipe.
51
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrography of a longitudinal section of the pipe showing that the carbon steel pipe is slightly banded and there is a decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
125
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The micrography of the welded joint between the flange and the shell, in a region that was through wall cracked, the fracture propagating in the shell plate base metal.
74
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Welded Joint
The micrography of a transverse section of the shaft shows the granular austenitic structure close to the surface of the shaft.
67
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - At the Surface

More from these cases

ML00106 — Inconel 718 Submarine BoltM - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
54
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
ML00105 — Inconel 718 Bolt of Special HeadM - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Low magnification micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of the bolt in a longitudinal section, in the center of the thickness. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
30
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Micrography close to the internal surface of a new tube, presenting casting defects.
47
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography close to the internal surface of the tube removed from service after 6 month, presenting high temperature oxidation and shrinkage voids (casting defects).
32
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography close to the external surface of the tube removed from service, damaged by high temperature oxidation.
25
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Micrographic detail of a longitudinal section of the base metal presenting a quenched and tempered microstructure.
49
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the low temperature heat affected zone of the pipe. The intercritical temperature (IC) is evident in the decorated grain boundaries of the previous austenite.
42
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the fusion line close to the cap pass (CP). The weld metal (non etched) is in the left side.
43
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the heat affected zone, a little far from the fusion line, close to the base metal.
40
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the fusion line in the center of the thickness, where the heat affected zone was reheated by the subsequent passes.
34
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line

+8 more from this case →

ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrography of a transverse section of the seam weld, close to the internal surface, presenting several cracks perpendicular to the thickness.
37
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrographic detail of the seam weld close to the internal surface, presenting the needles that are the result of microsctructural evolution and cracks filled with oxides.
36
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrography of a transverse section of the seam weld, in the middle of the thickness, presenting several parallel cracks.
27
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - In the Center of the Thickness
Micrographic detail of the seam weld in the middle of the thickness, presenting the needles that are the result of microsctructural evolution and cracks filled with oxides.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - In the Center of the Thickness

+6 more from this case →

ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrographic detail of the interface in the longitudinal section of the pipe showing the Vickers (300g) microhardness values, close to the interface in the carbon steel side and in the stainless steel side. Although the Nital etch does not allow to reveal the structure in the stainless steel side, the high hardness values show that the structure is different.
113
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrography of the interface between the carbon steel that is strongly etched by the electrolytic oxalic acid (in the left side of the figure) and the stainless steel, in the longitudinal section of the pipe. There is a strain hardened layer very close to the interface, at the stainless steel side.
79
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Longitudinal Section
ML00050 — Fatigue Failure of a 316SS Pressure StabilizerM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
The micrography of the welded joint between the flange and the shell, in a region that was not yet macroscopically cracked, presented a fatigue crack from the margin of the fillet weld.
71
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Welded Joint
ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Micrographic detail of the granular austenitic structure close to the surface of the shaft.
64
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - At the Surface
The micrography of a transverse section of the shaft shows a duplex grain size structure in the center of the shaft.
49
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - In the Center of the Thickness
The micrography of a transverse section of the shaft shows a duplex grain size structure in the center of the shaft. This conditions was probably generated due to the delta phase presented in segregated bands in the center of the original bar.
56
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - In the Center of the Thickness