Optical Microscope

6 cases · 72 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Sound Standard: API clear all

Optical Microscope — sub-branches

Chromic Acid Electrolytic Etched 6Kalling Etched Micrography by OM 13Nital Etched Micrography by OM 44Oxalic Acid Electrolytic Etch 9

Results

SortNewestOldestTitle A-ZTitle Z-A
Image by scanning electron microscopy of the metallurgically bonded interface of the internally cladded pipe. It is a longitudinal seam welded pipe, with substrate in low alloy steel X65 and clad plate in Alloy 625 (welded by a solid state process). The region is a detail in the side of the Ni alloy clad plate where a grain refinement has occurred probably due to recrystallization of a strain hardened region during later heat treatment. The microhardness of this region is a lot higher than the value obtained out of this region, in the clad plate.
904
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Oxalic Acid Electrolytic EtchDf - Clad Interface
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the core wire, 2.0 mm diameter, in the center of the thickness, showing a strain hardened structure, aligned.
113
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
431
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
45
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
The micrography of the pipe in the longitudinal section shows an aligned structure.
60
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal

More from these cases

ML00133 — Seam Welded Pipe Cladded with Alloy 625M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
48
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure,
50
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
55
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+10 more from this case →

ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
72
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure.
68
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
67
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image. Some decarburization of the low alloy steel substrate is evident since the microstructure is slightly different a little far from the interface.
66
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
59
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+7 more from this case →

ML00117 — High Carbon Steel Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Micrography of a longitudinal section of the core wire, 2.0 mm diameter, in the center of the thickness, showing a strain hardened pearlitic structure.
89
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the core wire, 2.0 mm diameter, in the center of the thickness, showing a strain hardened pearlitic structure.
81
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Strain hardened pearlite
Micrography of a longitudinal section of the core wire, 2.0 mm diameter, at the surface of the wire, showing that the wire presents no protective layer (not galvanized nor plated) and the microstructure is strain hardened, aligned.
71
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of a longitudinal section of the core wire, 2.0 mm diameter, at the surface of the wire, showing that the wire presents no protective layer (not galvanized) and the microstructure is strain hardened, aligned.
60
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the core wire, 2.0 mm diameter, at the surface of the wire, showing that it presents no protective layer (not galvanized nor plated) and the microstructure is pearlitic, strain hardened.
77
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - No Coating Layer

+12 more from this case →

ML00106 — Inconel 718 Submarine BoltM - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Micrography of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
63
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
54
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
49
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
ML00105 — Inconel 718 Bolt of Special HeadM - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
39
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
Micrographic detail of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
Low magnification micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrographic detail of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
26
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains

+3 more from this case →

ML00053 — SAW Longitudinal Seam of X70 PipeM - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Detail of the microstructure in the center of the plate, in the longitudinal section. The structure is refined and presents different ferritic grain sizes.
49
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Detail of the microstructure in the center of the plate, in the longitudinal section. The ferritic structure is refined and presents different grain sizes. Carbides are presented in different morphologies (perlite, precipitated) and there are probably microphases (aligned in a central segregation line).
55
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the fusion line of the second pass (not reheated). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
51
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Center of the weld in the second pass. Columnar grains of the previous austenite.
45
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Weld Metal
Fusion line of the first pass (reheated in high temperature). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
43
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line

+6 more from this case →