Optical Microscope

5 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Pipe Condition: Damage Microstructure: Austenite clear all

Optical Microscope — sub-branches

As polished micrography 4Glyceregia Etched Micrography by OM 6Micrography by OM 6Micrography by OM using A262 Method A 8

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the new tube close to a region of a casting defect (shrinkage), presenting only austenitic structure with a network of primary precipitates.
351
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Micrography of a longitudinal section of the pipe (seamless), that shows the through wall cracking, straigth and not associated to any welded region or microstructural problem.
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Through Wall Cracking
Micrography of the transverse section of the NEW TUBE, in the center of the thickness, showing the austenitic structure with primary carbides network.
410
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Longitudinal section of the main pipe showing as austenitic structure with small amount of delta ferrite, aligned. The white band in the center of the figure is a segregation band that was not fully etched.
133
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of a transverse section of the pipe, presenting the pitting corrosion. As polished.
310
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OMDf - Pitting

More from these cases

ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Micrography close to the external surface of a new tube, sound.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
Micrography close to the internal surface of a new tube, presenting casting defects.
47
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography of the tube removed from service after 6 month, close to a region of a casting defect (shrinkage), presenting austenitic structure with a network of primary precipitates (initial stage of coarsening) and intragranular secondary precipitation.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation
Micrography close to the internal surface of the tube removed from service after 6 month, presenting high temperature oxidation and shrinkage voids (casting defects).
31
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography close to the external surface of the tube removed from service, damaged by high temperature oxidation.
25
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Micrography of the pipe in a longitudinal section, close to the external surface, showing a pit (adjacent to the through wall cracking). The corrosion spt is not associated to any microstructural feature.
61
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Pitting
Micrography of a longitudinal section of the pipe presenting a granular austenitic structure, typical of a solid solution annealing condition. No carbide precipitation.
61
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Micrography of the transverse section of the NEW TUBE, close to the external surface, showing the austenitic structure with primary carbides network.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects close to the external surface.
49
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects in the center of the thickness.
47
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE, in the center of the thickness, showing the austenitic structure with primary carbides network and secondary precipitation.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE,close to the external surface, showing the austenitic structure with coalesced carbides and secondary precipitation.
39
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Longitudinal section of the main pipe showing as austenitic structure with small amount of delta ferrite, aligned (black dots).
116
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography transverse to the weld and to the fracture surface (right side of the figure).
116
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Fracture
Micrography of the section transverse to the weld and in a region close to the fracture surface (to the right side of the figure). The secondary fatigue microcracks are associated to the stress concentration raisers of the margin of the weld, irregular.
110
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Fatigue Crack
ML00014 — Pitting Corrosion in 316SS PipeM - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Austenitic structure at the transverse section of the pipe, free from carbides.
277
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Austenitic structure, free from carbides, exactly in the region of the pitting, indicating that the corrosion is not associated to the material microstructure.
261
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite