Optical Microscope

10 cases · 77 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Condition: Sound clear all

Optical Microscope — sub-branches

Kalling Etched Micrography by OM 31Micrography by OM using A262 Method A 12Micrography by OM, HF + HNO3 + H2O etch 6NaOH Electrolytic Etched Micro 16Nital Etched Micrography by OM 12

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
431
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
45
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the strain hardened austenitic structure in the longitudinal section of the bolt.
441
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the strain hardened austenitic structure in the longitudinal section of the bolt.
412
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of the tubing fusion line. The welding was conducted in two passes. The average hardness at the heat affected zone of the tubing is 257 HV5.
825
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line Left Side
Micrographic detail of the austenitic structure at the surface, where the grain size of the material increased. By optical microscopy the intragranular precipitation due to solution annealing and aging is not revealed.
794
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Base metal micrographic detail presenting a tempered martensitic microstructure.
27
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
The micrography of the pipe in the longitudinal section shows an aligned structure.
60
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal

More from these cases

ML00106 — Inconel 718 Submarine BoltM - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Micrography of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
63
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
54
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
49
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
ML00105 — Inconel 718 Bolt of Special HeadM - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
39
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
Micrographic detail of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
Low magnification micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrographic detail of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
27
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains

+3 more from this case →

ML00101 — High Strength 316SS BoltM - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
52
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
46
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
32
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
31
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrographic detail of the strain hardened austenitic structure at the thread.
25
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite
ML00087 — High Strength Austenitic SS BoltM - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
73
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
62
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
65
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
65
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrographic detail of the strain hardened austenitic structure at the thread.
59
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite
ML00100 — Superduplex Tubing to Forging Welded JointM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Micrography of the tubing heat affected zone.
69
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - HAZ Left Side
Micrography of the tubing heat affected zone.
68
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - HAZ Left Side
Low magnification micrography of the superduplex stainless steel tubing (base metal), in the longitudinal direction. Refined ferritic-austenitic structure. The average hardness in the section is 264HV5.
58
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Base Metal Left Side
Micrography of the superduplex stainless steel tubing (base metal), in the longitudinal direction. Refined ferritic-austenitic structure.
55
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Micrographic detail of the superduplex stainless steel tubing (base metal), in the longitudinal direction. Refined ferritic-austenitic structure.
53
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure

+10 more from this case →

ML00089 — Inconel 718 Allen Bolt for Subsea ApplicationM - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
The micrography of a longitudinal section of the bolt close to the surface, at the thread, shows that it was machined from a bar, not rolled.
37
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
The micrography of a longitudinal section of the bolt, in the center of the thickness (ND 1/2"), shows an equiaxial granular structure. Although the material was hardened by heat treatment (solution annealing and aging), the microstructure at this magnification does not reveal the intragranular precipitation.
34
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains
Micrographic detail of a longitudinal section of the bolt, close to the surface (ND 1/2"). The grain size is higher than the center of the bolt.
28
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Micrographic detail of the heat-affected zone close to the base metal.
29
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the heat-affected zone close to the fusion line.
31
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the tempered martesite weld metal close to the fusion line. The columnar grains can be observed .
22
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal
Micrography of the base metal showing a tempered martensitic microstructure.
30
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Micrography of the heat-affected zone. The fusion line is in the right and the coarse structure of the base metal is refined at the heat affected zone.
28
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone

+8 more from this case →

ML00053 — SAW Longitudinal Seam of X70 PipeM - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Detail of the microstructure in the center of the plate, in the longitudinal section. The structure is refined and presents different ferritic grain sizes.
49
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Detail of the microstructure in the center of the plate, in the longitudinal section. The ferritic structure is refined and presents different grain sizes. Carbides are presented in different morphologies (perlite, precipitated) and there are probably microphases (aligned in a central segregation line).
55
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the fusion line of the second pass (not reheated). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
51
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Center of the weld in the second pass. Columnar grains of the previous austenite.
45
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Weld Metal
Fusion line of the first pass (reheated in high temperature). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
43
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line

+6 more from this case →