Optical Microscope

4 cases · 45 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Engine Condition: Damage clear all

Optical Microscope — sub-branches

As polished micrography 9Micrography by OM 4Nital Etched Micrography by OM 26Oxalic Acid Electrolytic Etch 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the tubing showing a granular structure, austenitic.
52
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
98
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography of the thermal spray (TS) layer showing the different alloys, gray oxides and black voids. The Ni base TS alloy is of a yellow colour at the interface with the shaft substrate (in the left). The Cr base TS alloy appears white, similar to the shaft substrate. Longitudinal section of the shaft.
42
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
632
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides

More from these cases

ML00167 — Fatigue of a Flared Tubing ConnectionM - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Micrography of a longitudinal section of the tubing, showing the austenitic structure free from strain hardening and free from grain boundary carbides.
51
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrographic detail of the austenitic structure, free from strain hardening and free from grain boundary carbides.
54
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrography of a longitudinal section of the tubing where the fracture occurred. the left side is the outer diameter and the right side is the inner diameter.
37
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - At the Surface
Micrography of a longitudinal section of the flared tubing where the fracture occurred. The starting point of the fracture is associated to the external side of the tubing, where it was connected by a nut and there was a localized plastic deformation due to the fitting assembly.
33
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Transgranular Fracture
Micrographic detail of the localized plastic deformation due to the fitting assembly, in the region where the fatigue has started.
30
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Plastic Deformation
ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), in the center of the thickness. It is possible to see a mixture of large graphite flakes and rosette grouping flakes.
80
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - In the Center of the Thickness
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the external surface (left side). It is possible to see smaller graphite flakes, interdendritic .
79
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the External Surface
Micrography of the longitudinal section of the cylinder, at the internal diameter (left side of the figure), in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix.
50
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of the longitudinal section of the cylinder, at the internal diameter, in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix. It is important to mention that the flakes are almost interconnecting themelves.
47
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Graphite in Flakes
Micrography of the longitudinal section of the cylinder, at the internal diameter, in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix. It is important to mention that the flakes are almost interconnecting themelves.
48
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Predominantly Pearlitic

+19 more from this case →

ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Micrographic detail, as polished in a longitudinal section, of the interface between the shaft substrate and the thermal spray layer. In the left it is the shaft substrate also presenting parts of aligned inclusions (gray). In the center it is the Ni base TS alloy and in the right it is the Cr base TS alloy. There are also black voids and grey oxides.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
Micrography of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
32
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Micrographic detail of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Micrographic detail of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and (over) tempered structure. Longitudinal section.
35
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Shaft microstructure in the longitudinal section, showing aligned segregations typical of the material forming.
31
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

+4 more from this case →

ML00003 — Cast iron Engine Valve SeatsM - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
206
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
182
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
137
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure