Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Metallographic aspect of a longitudinal section of the clamp, at the surface (left side of the image) showing a region where there are corrosion pits in the carbon steel clamp, due to the lack of protection by the coating, and the propagation of small transgranular cracks from to the surface.
30
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Micrography by OMDf - Crack
Micrography of the plate in the middle of the thickness, showing the aligned structure tyical of a rolling process. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrography of the pin in a longitudinal section, transverse to the fracture surface, at the ductile final fracture, presenting microvoids connecting with plastic deformation of the structure.
50
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fracture
As polished micrography of the hydraulic line sample in the longitudinal section, close to the outer diameter, showing that the cracks are branched and thin, opened to the external surface.
58
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Micrography by OMDf - Close to the External Surface
Micrography of a longitudinal section of the bolt, as polished, presenting brittle cracks, transverse to the bolt axis.
1241
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Cracks
The micrography, in the "as polished" condition, of the longitudinal section of the bolt showing that there are non-continuous longitudinal cracks, intergranular, associated to regions of impurities, probably segregation bands, as evidenced by the grey elongated sulfide inclusions.
76
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Intergranular Cracking
Micrography of the pipe in a longitudinal section, close to the external surface, showing a pit (adjacent to the through wall cracking). The corrosion spt is not associated to any microstructural feature.
61
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Pitting
Micrography of the cast rim, base metal, in the as polished condition, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that sugegsts a solution annealed treatment.
120
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by OMDf - Base Metal

More from these cases

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography showing the alpha plus beta microstructure in the middle of the thickness. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
32
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the alpha (light grains as a matrix) plus beta (dark phase) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta phase (dark) in the alpha grains (light) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
24
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta (dark phase) in alpha microstructure. Etched with HF+ HNO3+H2O solution.
26
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrography by SEM of the plate in the middle of the thickness, showing the alpha microstructure (dark grains) and the beta phase (light). Etched with HF+HNO3+H2O.
35
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta

+12 more from this case →

ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
104
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Brittle Cracks
Micrography of a longitudinal section of the bolt, as polished, presenting brittle Intergranular and transgranular cracks, transverse to the bolt axis.
94
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Longitudinal Section
ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Micrographic detail of the cast rim, base metal, in the as polished condition, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that sugegsts a solution annealed treatment.
75
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by OMDf - Base Metal