Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Hydrides in Titanium Weld
1
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Micrography by OMDf - Hydride Formation
Metallographic aspect of a longitudinal section of the clamp, at the surface (left side of the image) showing a region where there are corrosion pits in the carbon steel clamp, due to the lack of protection by the coating, and the propagation of small transgranular cracks from to the surface.
30
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Micrography by OMDf - Crack
Micrography of a section tranverse to the pipe and to the weld between the 8"pipe and the 2" fitting weldolet. The crack starts exactly at the margin of the weld and propagates in the pipe longitudinal direction, in a straight line, not related to any metallurgical aspect.
30
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Cracking
Micrography of the plate section, close to the surface that suffered the impact. The projectile melted and created a film at the surface. HF+HNO3+H2O chemical etch.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Melted film
Micrographic aspect of the Cr layer at the surface presenting incipient damage. Microcracks of the Cr layer, associated to small pits.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Cracks
Micrography of the pin in a longitudinal section, transverse to the fracture surface, at the ductile final fracture, presenting microvoids connecting with plastic deformation of the structure.
50
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fracture
Micrography of the pin longitudinal section (transverse to the fracture), as polished. The fracture (in the top of the figure) is flat and it is possible to see secondary cracks with intergranular morphology.
40
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Secondary Cracks
Micrography of a longitudinal section of the bolt, as polished, presenting brittle cracks, transverse to the bolt axis.
1241
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Cracks

More from these cases

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Micrographic detail of the fatigue crack propagation in the pipe longitudinal direction, in a straight line, not related to any metallurgical aspect.
29
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Fatigue Crack
ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The projectile sheared the plate but did not perforate it, and the projectile materials (Cu and Pb) deposited at the .surface. HF+HNO3+H2O chemical etch.
9
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The projectile, impacted in the right side of the crack, sheared the plate but did not perforate it and created several longitudinal ductile secondary cracks. HF+HNO3+H2O chemical etch.
16
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack
Micrographic detail of the damaged plate (the side of the bullet impact is to the top of the figure). The projectile, in the right side, sheared the plate but did not perforate it and created longitudinal ductile secondary cracks in the middle of the thickness. HF+HNO3+H2O chemical etch.
11
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Secondary Cracks
Micrographic detail of the shearing of the material due to the projectile impact. It is a very localized effect. HF+HNO3+H2O chemical etch.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack
Micrography of the 3/8" thickness titanium alloy plate, in a section. The impact side of the plate is to the top of the figure. The plate was sheared through wall in a very localized position. HF+HNO3+H2O chemical etch.
6
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack

+6 more from this case →

ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
104
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Brittle Cracks