Kalling Etched Micrography by OM

3 cases · 22 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: API clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
431
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
45
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
13Cr SS longitudinal section micrography, at the collapsed region, showing a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
437
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00106 — Inconel 718 Submarine BoltM - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Micrography of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
63
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
54
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating that it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial.
49
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
ML00105 — Inconel 718 Bolt of Special HeadM - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Micrography of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
39
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
Micrographic detail of the bolt in a longitudinal section, at the bolt thread, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Machined Thread
Low magnification micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrographic detail of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
27
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains

+3 more from this case →

ML00039 — Collapse in Tubular 13CrM - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
13Cr SS in the longitudinal section, at the collapsed region. Non uniform structure (ferritic matrix and decorated prior austenite grain boundaries) that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
54
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
13Cr SS in the longitudinal section, at the collapsed region. Detail of the non uniform structure (ferritic matrix and decorated prior austenite grain boundaries) that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
48
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Prior Austenite Boundaries Decorated
13Cr SS in the transverse section, at the collapsed region, showing a non uniform structure that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
29
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
13Cr SS transverse section micrography, at the collapsed region, showing a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
29
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
The micrography of the 13Cr SS in the transverse section, at the collapsed region, shows a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
32
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Overtempered Structure

+3 more from this case →