Kalling Etched Micrography by OM

5 cases · 28 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Austenite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
17-4 PH rod. Micrography of the longitudinal section in the center of the thickness, presenting an aged martensitic structure. The darker lines are bands of (sligthly) segregated regions. This material presents properties that correspond to the H1150 grade.
73
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the forging material, presenting a granular austenite, precipitation hardened.
84
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
The stud presents an austenitic structure, with primary and secondary precipitates of a size that is visible in low magnification microscopy.
55
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Austenite
The micrography of a transverse section of the shaft shows the granular austenitic structure close to the surface of the shaft.
67
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - At the Surface
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
113
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite

More from these cases

ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
17-4 PH rod. Micrography of the longitudinal section in the center of the thickness, presenting an aged martensitic structure. The darker lines are bands of (sligthly) segregated regions. This material presents properties that correspond to the H1150 grade.
66
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched Micrography by OMDf - Martensite
17-4 PH rod. Micrographic detail of the aged martensitic structure. At this magnification level the previous austenite grain boundaries are evidenced. It is also possible to see that the bands of (sligthly) segregated regions are all martensitic.
64
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched Micrography by OMDf - Martensite
17-4 PH rod. Micrography of the longitudinal section close to the surface, presenting the roughness (the waves at the surface) and a region where a pitting was still in the beginning, not related to any specific microstructure.
70
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched Micrography by OMDf - Pitting
ML00078 — Hydrogen Cracking of IN 718 Subsea ConnectorM - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the conector, at the fracture position, showing secondary cracks from the fracture surface.
63
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
The micrographic detail of the longitudinal section at the fracture surface shows intergranular morphology for the secondary cracks (longitudinal to the forging axis).
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks.
54
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
48
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
ML00075 — Hydrogen Cracking of IN 718 Subsea FastenersM - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
The stud structure evidences grain boundaries precipitation of probably delta phase (an overaging of the hardening precipitate).
49
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrography of a longitudinal section of the stud, at the fracture surface, in the thread.
44
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
Micrographic detail of a longitudinal section of the stud, at the fracture surface, in the thread. It is possible to see primary precipitates (yellow) already cracked and intergranular propagation.
37
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrography of a longitudinal section of the stud, at the fracture surface in the center of the thickness, showing a long secondary cracking (vertical in the left).
35
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of the longitudinal section of the stud, at the secondary cracking.
26
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Brittle Cracks
ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Micrographic detail of the granular austenitic structure close to the surface of the shaft.
64
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - At the Surface
Granular austenitic structure close to the surface of the shaft.
61
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - Austenite
The micrography of a transverse section of the shaft shows a duplex grain size structure in the center of the shaft.
49
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - In the Center of the Thickness
The micrography of a transverse section of the shaft shows a duplex grain size structure in the center of the shaft. This conditions was probably generated due to the delta phase presented in segregated bands in the center of the original bar.
56
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - In the Center of the Thickness
Duplex grain size structure, austenitic. The small grains are probably due to the arresting effect of the delta phase during fabrication in high temperature.
47
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - Duplex structure

+2 more from this case →

ML00011 — Intergranular SCC of Pure NickelM - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
110
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
96
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Crack propagation with intergranular and transgranular aspects.
55
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Corrosion Cracking
Crack propagation with intergranular and transgranular aspects.
45
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Corrosion Cracking