Aspect Before Analysis

27 cases · 77 images for “corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the tube internal surface after removal from the boiler, presenting multiple longitudinal cracks.
295
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
Aspect of a crevice corrosion of the flange, under the bolt head, showing evidences that the cathodic protection system was not connected to the stainless steel instrument.
1434
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Localized Corrosion
Aspect of the Nitronic 60 cylinder, OD 36.4mm, presenting pits at the external surface.
219
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the pin surface, presenting multiple cracks, paralel to the fracture position.
122
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Multiple cracks
Drilling tool that broke close to the region of the male connector (pin end). The fracture is at the right side of the figure.
102
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Region of the leakage close to the welded joint between the pipe and the 90° elbow, in the 1 1/2" nominal diameter piping, SCH 40 (3.7 mm thick). See the schematic drawing in the next figure
966
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Aspect Before AnalysisDf - Leakage

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Detailed aspect of the fractured position, in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
86
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Same aspect of the previous image after cleaning, showing a subcritical propagation aspect (fatigue), starting at the groove (ID) and also at the clamp surface in the OD.
75
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
In the region where the polimeric insert was loose, the protective coating of the clamp has suffered detachment.
69
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Layer Detachment
Close to the ID of the clamp, at the groove position, there are cracks in the coating (white brown) and also at the substrate.
63
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Cracks

+3 more from this case →

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Aspect of the external surface of the leaking tube, after removal of the membrane.
262
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - External Surface
ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Aspect of the internal surface of the pipe after cutting, showing the colors of the internal deposits and the leaking line associated to the pipe seam.
288
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Leakage
Aspect of the internal surface of the pipe after cleaning, showing the leakage line.
67
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface
Detailed aspect of the internal surface of the pipe after cleaning, in a region where the pipe was leaking.
62
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Leakage
ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Flanged case, 640mm long. The photo presents a general view of the instrumentation system, destroyed after only 6 months in subsea service. The system was manufactured using only 316 stainless steel and the case was 20 mm thick.
335
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - General View
Aspect of the instrument system after disassembling. The internal part of the case, where the electronic device was operating, was wet by seawater and failed to send signals to the surface.
258
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - General View
Detail of the electronic device after removing the external case. It is corroded because seawater entered in the equipment that was pressurized from the external sea environment.
228
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Corrosion
The case where the electronic device was installed suffered a localized corrosion that allowed the seawater to wet the internal side, destroying it. The position where the leakage occurred originally presented a hole that was sealed with a plug and the corrosion occurred in a crevice condition.
166
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Localized Corrosion
ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Aspect of the 17-4 PH rod, OD 10.6 mm, presenting deep pits at the external surface.
125
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface
ML00085 — Corrosion Fatigue of a Martensitic SS PinM - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Aspect of the 5/8" diameter pin, that was 3" long and broke close to the center.
104
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Typical fatigue fracture, reversed bending.
74
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
ML00082 — Corrosion Fatigue of a Drilling ToolM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
The fracture was removed from the failed part and analyzed separately. The aspect of the fracture surface is presented. It is flat, with regions of fatigue propagation and with regions of erosion by washout (to the right side of the figure).
80
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Detail of the fracture surface presenting a fatigue propagation from the outside of the tool.
69
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Detail of the fracture surface presenting erosion by a washout, because the equipment was pressurized when the cracking became through wall.
63
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Washout
ML00065 — Erosion Corrosion of Monel PipingM - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Aspect of the piping cut in the longitudinal direction, presenting the leakage region close to the welded joint between the pipe and the 90° elbow. The original SCH 40 (3.7 mm thickness) presents an actual average thickness of 2 mm all through the piping extension, evidencing a general thinning. See the schematic drawing in the next figure.
364
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Aspect Before AnalysisDf - Leakage