Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Kalling Etched Micrography by SEM clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the original casting blade structure. The tempered martensite is more clearly revealed by the scanning electron microscopy. The average hardness level measured in this side is 270 HV.
70
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side

More from these cases

ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Higher magnification of the martensitic structure of the original casting blade structure, hardness level of 270HV10.
26
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Micrographic detail of the inserted casting structure. The martensite presents a less tempering aspect than the original casting revealing that it was heat treated in a different condition. The average hardness level measured in this side is 370 HV.
157
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Higher magnification of the martensitic structure of the inserted casting structure, hardness level of 370HV10.
23
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Micrographic detail of the original casting blade fusion line, presenting the tempered martensitic structure similar for the HAZ (left side of the figure) and the weld metal (right side of the figure).
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Fusion Line Left Side
Micrographic detail of the original casting blade fusion line, presenting the tempered martensitic structure similar for the HAZ (left side of the figure) and the weld metal (right side of the figure).
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Fusion Line Left Side

+7 more from this case →