Boiler

6 cases · 30 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: A Capture method: Optical Microscope Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the longitudinal section of the tube, close to the external surface, presenting a thick deposit.
102
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Scale
Micrographic details of the longitudinal section of the tube, close to OD, showing paralel cracks, filled with oxides, perpendicular to the surface.
115
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrography of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks started from the internal surface of the steam drum.
94
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Typical branched stress corrosion cracks in a low carbon steel, ferritic-pertlitic structure. The cracks are filled with corrosion products.
771
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
A small sample was removed from the steam drum and the micrography shows that the cracks are intergranular (previous austenite) and located in the weld metal.
285
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell in the internal side, using an unsuitable welding procedure that created a too high hardness HAZ.
123
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks

More from these cases

ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrographic detail of the longitudinal section of the tube, close to the internal surface, presenting a thick deposit.
94
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Scale
Micrography of the longitudinal section of the tube, close to the internal surface. A thick scale is evident, but no microstructural changes compared to the center of the tube.
78
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Scale
ML00104 — Thermal Fatigue of a Boiler TubeM - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Micrographic details of the longitudinal section of the tube, close to OD, showing paralel cracks, filled with oxides, perpendicular to the surface.
109
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Thermal Fatigue Cracks
Micrographic details of the longitudinal section of the tube, close to ID, showing paralel cracks, filled with oxides, perpendicular to the surface.
103
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrographic details of the longitudinal section of the tube, close to ID, showing paralel cracks, filled with oxides, perpendicular to the surface.
99
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Thermal Fatigue Cracks
Micrography of the longitudinal section of the tube, close to OD, showing the cracks from the surface. The cracks are filled with oxides and slightly opened by corrosion.
84
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Thermal Fatigue Cracks
Micrography of the longitudinal section of the tube, close to ID, showing the cracks from the surface. The cracks are filled with oxides and there is still a layer of oxides at the internal surface, detached from the surface (probably during cleaning).
76
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Thermal Fatigue Cracks
ML00019 — Transgranular SCC in Boiler Steam DrumM - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Micrographic detail of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks presented a transgranular morphology
86
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
Micrographic detail of the transgranular stress corrosion cracking.
80
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
Micrographic detail of the transgranular stress corrosion cracking.
157
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
ML00018 — SCC in Boiler Steam DrumM - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Micrography of the crack at the internal surface of the steam drum. The shell plate presents a ferritic perlitic structure.
162
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, in a sample as polished, presenting the opened crack.
144
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks
Stress corrosion cracks propagating in the ferritic-perlitic structure.
120
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, as polished, presenting the cracks filled with corrosion products.
100
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks
Micrographic detail of a crack, in a sample as polished, presenting regions of opened cracks and filled cracks.
88
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks

+1 more from this case →

ML00020 — Intergranular SCC in Boiler Steam Drum RepairM - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
The micrography of the small sample removed from the steam drum shows that the cracks are intergranular (previous austenite) and located in the weld metal.
274
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
Secondary cracks in the weld metal showing an intergranular morphology. Stress Corrosion Cracking.
249
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
Detail of the secondary cracks in the weld metal with intergranular morphology. Stress Corrosion Cracking.
251
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
Detail of the intergranular stress corrosion cracking of the drum shell weld repair.
217
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
ML00008 — Cold Cracks in CMn Steel Pressure VesselM - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell in the internal side, using an unsuitable welding procedure that created a too high hardness HAZ. The cracks are mainly located at the fusion line.
118
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell in the internal side, using an unsuitable welding procedure that created a too high hardness HAZ. Several internal cracks at the fusion line.
101
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell using an unsuitable welding procedure, with a low preheating and no PWHT. Cracks propagated in the heat affected zone.
99
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell using an unsuitable welding procedure, with a low preheating and no PWHT. Cracks propagated in the weld metal.
100
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks