Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Standard: ASTM Detail focus: External Surface clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Circumferential weld aspect. Two passes in the cap. This forging to pipe welded joint, 22 mm thick, was welded by an automatic process in a narrow gap. The pipe is to the top of the image and the forging is to the bottom of the image.
165
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - External Surface
Image of the external surface of the valve body at the region where the Alloy 625 insert was fillet weld to the SDSS valve body. The surface was later machined, so it is possible to see only a mark indicating where the weld is. The brittle crack is arrested at the margin of the weld. It is possible to see strong deformation at the crack tip when it arrives the weld.
41
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the external surface of the tube, presenting a large circunferential crack.
171
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Surface AspectDf - External Surface