Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 182 Detail focus: Crack clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Transverse section of the 14" pipe in the center of the 2" branch using a weldolet fitting welded to the main pipe. The internal side of the pipe is to the top of the figure and the through wall fatigue cracking is located at the margem of the weld. It is possible to see that it is a full penetration weld and the fitting thickness is several times larger than the pipe thickness.
174
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Electrolytically Etched MacroDf - Crack
Micrographic detail of the through wall cracking in the middle of the thickness, showing that the cracking is associated to ferrite network in the (super)duplex microstructure.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Micrography by SEMDf - Crack

More from these cases

ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Micrographic detail of the cracking, associated to the ferrite network, that presents both corrosion (preferential dissolution) and fracture (clevage) aspects.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Electrolytic Etch Micrography by SEMDf - Crack