Atlas

6 cases · 29 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Used Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the coaster surface grooves, by scanning electron microscopy in a low magnification, showing in the right side the flat region that serves as a support; and in the left side the decorative grooves. The smooth surface in the groove suggests that the coasters were manufactured by casting.
66
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Micrographic detail of the pearlitic structure in the center of the shaft thickness.
82
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by SEMDf - Pearlite
Low magnification micrography of the welded region, showing the interface between the base in the bottom and the fusion zone (between the liquidus and solidus temperatures), as well as the weld metal in the top. There are pores close to the weld metal and in the fusion zone the interdendritic space was melted and the eutectic morphology was changed. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Repair
Micrographic detail of the original casting blade structure. The tempered martensite is more clearly revealed by the scanning electron microscopy. The average hardness level measured in this side is 270 HV.
70
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Image by scanning electron microscopy of the metallurgically bonded interface of the composite seamless tube (carbon steel externally claded with stainless steel), in the side of the stainless steel where a strain hardening effect plus a carbide precipitation in twins is shown. The hardness of this region (279 HV0.3) is a lot higher than the value obtained out of this region (167 HV0.3) for the same stainless steel.
814
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure and detrimental phases associated to the ferritic structure.
47
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Duplex structure

More from these cases

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Detail of the previous photo showing the flat surface in the right side and the grooves in the left side. The flat side is scratched and the grooves presented a smooth finishing (with dendritic morphology).
57
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the flat scratched region of the coaster surface. The dark grey "nodules" are lead (Pb) base inclusions.
50
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the groove region, showing a typical casting morphology at the surface: smooth and presenting a dendritic aspect with interdendritic shrinkage. Some dark grey "nodules" with Pb inclusions are also observed.
51
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
There are some regions in the coaster surface where pores associated to shrinkage is evident.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - Casting defects
ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Micrographic detail of the cast rim at the heat affected zone presenting coalesced Si particles at the interdendritic space an neddles of Fe rich phase. Keller etch.
47
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Heat Affected Zone
The coalesced silicon particles in the interdendritic space of the base metal presents a remelting at the fusion zone. The micrography by SEM shows the exactly line where the eutectic is remelted and refined. Keller etch.
40
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Fusion Line
Refined dendrites in the weld metal. The Si/Al alpha eutectic in the interdendritic space is also refined. Keller etch.
38
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Metal
Hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology.
37
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks
Detail of the hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Higher magnification of the martensitic structure of the original casting blade structure, hardness level of 270HV10.
26
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Micrographic detail of the inserted casting structure. The martensite presents a less tempering aspect than the original casting revealing that it was heat treated in a different condition. The average hardness level measured in this side is 370 HV.
157
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Higher magnification of the martensitic structure of the inserted casting structure, hardness level of 370HV10.
23
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Micrographic detail of the original casting blade fusion line, presenting the tempered martensitic structure similar for the HAZ (left side of the figure) and the weld metal (right side of the figure).
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Fusion Line Left Side
Micrographic detail of the original casting blade fusion line, presenting the tempered martensitic structure similar for the HAZ (left side of the figure) and the weld metal (right side of the figure).
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Fusion Line Left Side

+7 more from this case →

ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
The scanning electron microscopy image details the strain hardened layer with carbide precipitation at twins, in the stainless steel side very close to the interface.
81
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Strain Hardened
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure and detrimental phases associated to the ferritic structure.
39
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Duplex structure