Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Welding Microstructure: Tempered Martensite Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the 4130 steel, normalized and tempered. The structure is sligthly banded (segregated) and the average hardness level is 20 HRc.
92
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the base metal presenting a banded microstructure in the longitudinal section of the pipe.
51
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Base metal micrographic detail presenting a tempered martensitic microstructure.
27
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal

More from these cases

ML00102 — AISI 4130 Forging Welded and OverlaidM - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Micrography of the 4130 steel, normalized and tempered. The microstructure is bainitic.
88
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the bainitic structure of the 4130 steel, normalized and tempered.
87
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
66
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
61
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the bainitic heat affected zone (HAZ) of 4130 forging at the Inconel overlay.
50
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainitic Ferrite

+6 more from this case →

ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Micrographic detail of a longitudinal section of the base metal presenting a quenched and tempered microstructure.
49
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the low temperature heat affected zone of the pipe. The intercritical temperature (IC) is evident in the decorated grain boundaries of the previous austenite.
42
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the fusion line close to the cap pass (CP). The weld metal (non etched) is in the left side.
43
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the heat affected zone, a little far from the fusion line, close to the base metal.
40
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the fusion line in the center of the thickness, where the heat affected zone was reheated by the subsequent passes.
34
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line

+8 more from this case →

ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Micrographic detail of the heat-affected zone close to the base metal.
29
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the heat-affected zone close to the fusion line.
31
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the tempered martesite weld metal close to the fusion line. The columnar grains can be observed .
23
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal
Micrography of the base metal showing a tempered martensitic microstructure.
30
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Micrography of the heat-affected zone. The fusion line is in the right and the coarse structure of the base metal is refined at the heat affected zone.
28
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone

+8 more from this case →