Atlas

2 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Used Microstructure: Tempered Martensite Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the wheel in the center of the thickness. The material presents a coarse structure.
88
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite. The tempering was in low temperature since the hardness is high (58 HRc at the surface).
87
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Uniform Structure

More from these cases

ML00158 — Surface Hardened Carbon Steel WheelM - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Micrography of the wheel in the center of the thickness, presenting a predominantly pearlitic structure and average hardness abot 196HB.
74
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrographic detail of the coarse pearlitic structure in the center of the wheel thickness. The part presents a wrought structure.
73
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrography of the wheel at the surface that was quenched and tempered. The material presents a tempered martensitic structure, with hardness that varied from 327HB to 363HB.
55
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the wheel at the hardened surface, presenting a refined martensitic structure, tempered for average hardness of 346 HB.
50
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic detail of the tempered martensitic structure.
50
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Martensite

+3 more from this case →

ML00084 — Walrus Tool SteelM - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Micrographic detail of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite, with small secondary carbides. The hardness in the section is 59 HRc.
73
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Martensite