Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Segregation Bands Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography presenting segregation bands in a martensitic structure. In the segregated regions the Nital etch effect is lower and the bands appear lighter. The black spots and lines are inclusions (some elongated) in the band.
91
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a transverse section of the spring, at the surface showing pits full of deposits.
36
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Transverse Section
Low magnification micrography of a longitudinal section of the valve body, in the center of the thickness. As expected for this high strength steel, the microstructure is martensitic, but with segregation bands.
48
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Banded Structure
Tempered martensite of the pipe body of this API 5D grade S135 drill pipe. The material presents, at this low magnification micrographic aspect, a slightly banded structure, usual for this type of drill pipe.
58
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Banded Structure
Longitudinal section micrography in a position of the thread, far from the failure. The stud presented a quenching and tempering structure and the thread was machined.
84
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Micrography of a longitudinal section of the bolt, as polished, presenting brittle cracks, transverse to the bolt axis.
1241
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Cracks
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking

More from these cases

ML00182 — Brittle Fracture of a LAS Fixing RodM - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Micrography presenting segregation bands (less etched) in a tempered martensitic microstructure.
81
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Segregated Regions
Micrography presenting a tempered martensitic microstructure, with light etch in segregated bands.
74
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
Low magnification micrography, revealing (in black) the impurities in the segregated bands.
63
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Longitudinal Section
Micrographic detail of the segregated bands.
61
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Segregated Regions
Micrographic etch for revealing previous austenite grain boundaries, that shows the impurities.
54
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Segregated Regions

+1 more from this case →

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
BASE METAL SURFACE - The micrography (transverse to the tube) presents the ferritic/pearlitic/bainitic structure.
75
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Granular structure
BASE METAL SURFACE - The microstructure of the base metal is ferritic/pearlitic/bainitic.
74
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Grain refined structure
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ
HAZ SURFACE
66
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ
HAZ SURFACE
55
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Bainitic HAZ

+18 more from this case →

ML00172 — Brittle Fracture of a LAS Valve SpringM - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Micrographic detail of the transverse section of the spring, at the surface, showing the pits full of corrosion deposits.
31
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Surface Deposits
Micrographic detail of spring surface, showing the pits full of corrosion deposits and a small decarburized layer (probably from the manufacturing processes).
30
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Decarburized Surface
Micrography of a longitudinal section of the spring, at the surface, indicating that there are multiple intergranular cracks initiating from the pit.
26
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Multiple cracks
Micrographic aspect of the multiple intergranular cracks, initiating from the bottom of a pit.
25
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of the intergranular cracks, initiating from the bottom of a pit.
29
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking

+3 more from this case →

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrography of a longitudinal section of the valve body presenting a martensitic microstructure. The structure is banded and the darker regions show inclusions (grey sulfides).
50
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the martensitic microstructure, in the longitudinal section. The hardness of the valve body is 34 HRc (Rockwell C) all through the thickness.
47
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Macrography of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. The valve body is 40 mm thick at this position and it is possible to see that at this position only one region is welded in repair, close to the outer surface (top), and there is a crack, transverse to the thickness, that is difficult to see with this magnification and that is clearly the propagation in fatigue.
47
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fatigue Crack
Low magnification micrography at the weld repair close to the internal surface of the valve body, in a longitudinal section. Weld metal to the bottom and heat affected zone to the top.
42
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Weld Repair
Micrography of the weld repair at the fusion line. Weld metal to the right and heat affected zone to the left.
37
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line

+18 more from this case →

ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body. Uniform structure.
45
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the pipe, at the thicker part of the fracture, showing several secondary cracks opened to the external side of the pipe. There are no problems in the material structure and the cracks are associated to large plastic deformation.
36
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of the secondary cracks opened to the external side of the pipe. The cracks are associated to large plastic deformation.
30
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of the ductile secondary cracks in the pipe body, close to the fracture. The strong plastic deformation is associated to the compression stresses generated by the buckling.
27
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Plastic Deformation

+3 more from this case →

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Microstructure of the stud in the longitudinal section, presenting segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration.
69
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Microstructure of the stud in the longitudinal section, out of a region of segregation, where the tempered martensitic microstructure appears more uniform.
72
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration. The localized microhardness (50g) in the band showed levels about 540HV, and out of the band, in the same localtion, presented an average hardness of 321 HV, indicating that the material is non uniform in the regions where there are bands.
66
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrographic detail of the martensitic structure of the stud in the longitudinal section, out of a region of segregation, where the microstructure appears more uniform and the microhardness is about 370HV (50g).
62
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Low magnification micrography of a stud longitudinal section in the first thread fillet adjacent to the fracture, presenting a large secondary crack without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
47
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+17 more from this case →

ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
104
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Brittle Cracks
Micrography of a longitudinal section of the bolt, as polished, presenting brittle Intergranular and transgranular cracks, transverse to the bolt axis.
94
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the bolt, showing the (secondary) crack propagating, transverse to the bolt, from a thread fillet.
91
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the (secondary) crack propagating transverse to the bolt, from a thread fillet.
91
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the (secondary) crack propagating transverse to the bolt, from a thread fillet.
80
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

+5 more from this case →

ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
The liquation crack is a hot crack in the base metal (at the HAZ) that induces a solidification crack in the weld metal.
66
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrographic detail of the cracks at the fusion line of the welded joint, at the connector side. The cracking presents morphology of melting regions of impurities at grain boundaries of the large grains of the heat affected zone (HAZ).
57
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
48
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
43
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
Micrography of the AISI 4130 forging, 5/8" thickness, close to the welded region, in the longitudinal section.
42
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal Left Side

+7 more from this case →