Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austenite Capture method: Kalling Etched Macro clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
17-4 PH rod, tubular, OD 10.6mm, wall thickness about 3.5 mm. Macrography of the rod in a transverse section showing the pitting in a position where it is almost through wall.
86
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched MacroDf - Pitting
The macrography shows the longitudinal section of the allen bolt, 1/2" nominal diameter, that was machined from a heat treated bar (solution annealed and aged). The granular structure presents differences in the grain sizes. At the bolt head (external surface of the original bar) the austenitic grain size is larger than in the center of the bar where the particles in segregated bands "arrested" the grains during hot forming and solution annealing.
58
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched MacroDf - Machined Thread
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
49
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Intergranular Cracking
The macrography of a transverse section shows the carbon steel tube, externally cladded with stainless steel. The tube was removed from service where it was welded to other tubes to form a wall.
156
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Kalling Etched MacroDf - Transverse Section
Macrography of the NEW TUBE, centrifugally cast, in the transverse section, presenting columnar grains close to the external surface.
50
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section

More from these cases

ML00089 — Inconel 718 Allen Bolt for Subsea ApplicationM - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Micrographic detail of a longitudinal section of the bolt, in the center of the thickness (ND 1/2"). Although the material was hardened by heat treatment (solution annealing and aging), the microstructure observed by optical microscopy does not reveal the intragranular precipitation.
33
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched MacroDf - Austenite
The micrography of a longitudinal section, at the bolt head close to the surface of the original bar. In this region the material increased the grain size due to the lack of particles (inclusions), to "arrest" the grain boundaries (during hot forming and solution annealing). The smaller grain size is located in the center of the bar, that concentrated the inclusions.
30
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched MacroDf - Dual grain sizes
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Macrography of the TUBE REMOVED FROM SERVICE, centrifugally cast, in the transverse section, presenting thickness loss and macrostructure deterioration.
33
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section