Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic Standard: A Capture method: Aspect Before Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. The cracking started at the margin of the weld in the upper part of the pipe, where the weld crossed the longitudinal direction of the pipe, perpendicular to the branch.
932
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Aspect of the external side of the connector, with a longitudinally crack of a brittle aspect. It is a 5/8" connector (15.8 mm).
134
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Steam drum presenting cracks in the shell, connecting tube holes.
1704
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Cracking
Seam welded tube, nominal diameter 2 1/4" and thickness 1/16".
105
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - Autogenous Weld

More from these cases

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Gas piping. Aspect of a branching line 2" ND with a flange, lateral to a main pipe ND 8", welded using a weldolet. The cracking is at the margin of the weld.
115
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
ML00103 — Brittle Fracture of a Free-Cutting ConnectorM - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Aspect of the internal side of the connector. The fracture, in the longitudinal direction, presents a brittle aspect. The thickness of the connector is about 2 mm.
126
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the brittle fracture, in the longitudinal direction.
105
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture