Atlas

1 case · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Segregation Bands Capture method: As polished micrography Detail focus: Fatigue Crack clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography in low magnification, as polished, of the crack in the valve thickness, showing the straight aspect of the fatigue propagation.
24
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrography, as polished, of the crack in the valve thickness, showing the straight aspect of the fatigue propagation.
22
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack
Micrographic detail of the straight crack that propagated by a fatigue mechanism.
18
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack
Cross-section showing a single jagged crack propagating through the matrix, with a small non-metallic inclusion nearby.
1
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack