Atlas

2 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Mechanical Industry Condition: Used clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the serrated walrus tool, interchangeable, that was removed at the end of its life. Dimensions of 1" thick, 2" width, 3" long.
419
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
The shaft presented a light wear at the end of the life. See the schematic drawing in the next figure
597
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00084 — Walrus Tool SteelM - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Micrography of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite. The tempering was in low temperature since the hardness is high (58 HRc at the surface).
87
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Micrographic detail of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite, with small secondary carbides. The hardness in the section is 59 HRc.
73
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Martensite
ML00064 — SAE 1045 Steel ShaftM - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Schematic drawing presenting the Shaft
168
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Identification drawingDf - At the Surface
Micrography of the longitudinal section of the shaft, in the center of the thickness, presenting a ferritic-perlitic structure typical of a hot forming process.
148
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of the ferritic-perlitic structure, typical of a hot forming process, in the center of the thickness.
138
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of the ferritic-perlitic structure, typical of a hot forming process, in the center of the thickness.
115
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the longitudinal section of the shaft, at the damaged surface (with a light wear). In low magnification the ferritic perlitic texture reveals the forging lines.
101
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface

+1 more from this case →