Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: FPSO Condition: Preferential Dissolution clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Visual aspect from the external side of the 14"ND flange butt welded to a pipe, presenting a through wall crack about 5mm to 10mm from the butt welding.
925
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Through Wall Cracking

More from these cases

ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
External surface aspect of the flange showing preferential dissolution, responsible for nucleation of the through wall cracking.
245
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Preferential Dissolution
Detail of the region at the flange external surface where the material is suffering the preferential corrosion.
177
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Preferential Dissolution
Macrography of a longitudinal section of the flange to pipe weld, cracked in the flange. Pipe thickness, measured, is 5 mm. Flange thickness at the welded region is 7.5 mm. The macro was etched using NaOH solution, electrolytic.
181
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MacroDf - Longitudinal Section
Macrography transverse to the circunferential weld, longitudinal to the piping, presenting the location, a little far from the welded joint margin, where the through wall cracking is positioned.
160
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MicroDf - Through Wall Cracking
Longitudinal section micrography at the cracked position, close to the external surface of the flange, showing cracks transverse to the thickness, associated to the microstructure.
147
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MicroDf - Cracks Transverse to the Surface