UNS

3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Preferential Dissolution Capture method: Aspect Before Analysis clear all

UNS — sub-branches

C28000 1C68700 1S32750 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Visual aspect of the internal side of the tube, after longitudinal cut, presenting regions where the internal layer is fully stained.
55
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the CuZn platesheet where it is corroded (cooling medium side). The (hot) air cooler uses treated seawater as the cooling medium and the corroded regions are associated to the regions in the heat exchanger of higher temperatures, and the leakage occurred in regions of contact of the platesheet to cooper alloy tubes.
1167
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Corrosion
Visual aspect from the external side of the 14"ND flange butt welded to a pipe, presenting a through wall crack about 5mm to 10mm from the butt welding.
925
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Through Wall Cracking

More from these cases

ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
After a longitudinal section of the flange to pipe weld, the through wall cracking opened in two parts and the fracture surface was analyzed. The flange side fracture surface is presented in this figure.
126
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Fracture