Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure clear all

B — sub-branches

16 1265 1348 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The plate longitudinal section presents a granular refined structure. Biphasic.
340
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Grain refined structure
The bar presented a large prior beta grain size and acicular alpha. Biphasic structure.
420
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Coarse Structure
The fracture micromechanism is ductile for the pin that has been sheared in a condition of controlling the load carrying. Elongated Dimples.
453
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Fractography by SEMDf - Elongated Dimples

More from these cases

ML00029 — Titanium Plate for Subsea ApplicationM - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Alpha and beta phases. Refined Structure.
52
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
Alpha and beta phases. Refined Structure.
46
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
ML00028 — Titanium Bar for Subsea ApplicationM - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
The bar presented alpha plus beta phases, acicular alpha and coarse prior beta grains.
97
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
Acicular alpha structure in a biphasic alloy of a large prior beta grain size. 4" diameter bar.
100
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Acicular Alpha
ML00007 — Free Machining Brass in Shear PinM - BrassP - Machined PartAp - LiftingCd - Shear
Uniform structure of the 1" shear pin all through the section. The edge is the fracture surface.
108
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - FeCl3+HCl+H2O solution Etched MacroDf - Longitudinal Section
The fracture surface is flat and smashed due to the shearing action.
87
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Aspect Before AnalysisDf - Fracture
The fracture surface is ductile and the micromechanism is dimples, elongated due to the shearing action.
83
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Fractography by SEMDf - Ductile Fracture
The micrography of the pin far from the fracture surface shows a biphasic brass, and Pb inclusions that are intentional to give a free machining condition for the alloy.
76
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - FeCl3+HCl+H2O Etched MicroDf - Two phases
The micrography of the pin at the fracture surface shows a strong plastic deformation as expected during shearing.
70
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - FeCl3+HCl+H2O Etched MicroDf - Plastic Deformation