ASTM

4 cases · 14 images for “brittle fracture”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Fracture clear all

ASTM — sub-branches

A 6

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Visual aspect of both sides of the fractures. They present a macroscopically brittle aspect, with chevron marks indicating the starting point at the thinner edge of the thread.
81
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
Micrography of a transverse section, perpendicular to the fracture surface, showing lack of plastic deformation during rupture.
50
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Aspect of the fracture surface, showing a brittle morphology. Flat fracture with chevron marks from regions close to the internal diameter of the padeye, where there are secondary cracks.
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Observing in higher magnification it is possible to see that the fracture presents a mixture of ductile and brittle micromechanisms. The intergranular mechanism indicates that the material is embrittled and the dimples indicate localized overloading conditions.
32
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Fracture
Detail of the ductile dimples and the brittle intergranular micromechanisms. This evidence (a mixture of mechanisms) suggests that the embrittlement is localized in some regions of the material.
34
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fractography by SEMDf - Fracture
Micrography of the nut in the longitudinal section, transverse to the fracture (top of the image).
15
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Fracture
Micrography transverse to the fracture (top of the image) showing no relationship with the bands.
15
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Fracture
ML00103 — Brittle Fracture of a Free-Cutting ConnectorM - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Micrography of a transverse section, perpendicular to the fracture surface, showing lack of plastic deformation during rupture.
45
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography of a transverse section, perpendicular to the fracture surface, showing lack of plastic deformation during rupture. Cleavage factes are evident in the ferritic structure close to the fracture surface.
47
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Micrography transverse to the fracture surface (in the top of the figure). The fracture is brittle and follows the interdendritic spaces, since these regions where the positions where there were casting defects.
14
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrographic detail of a transverse section, at the fracture (in the top of the figure). The fracture is brittle and follows the voids at interdendritic spaces, with secondary cracks.
12
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrographic detail of a transverse section, at the fracture (in the top of the figure). The fracture is brittle and follows the voids at interdendritic spaces, with secondary cracks.
10
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture