Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Detail focus: Close to the External Surface clear all

ASTM — sub-branches

A 50B 7F 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the external surface (left side). It is possible to see smaller graphite flakes, interdendritic .
79
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
43
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
33
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of the longitudinal section of the tube, close to the external surface, presenting a thick deposit.
110
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Close to the External Surface
The micrography of the longitudinal section of the tube, close to OD, shows the paralel cracks, filled with oxides, perpendicular to the surface.
1444
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Close to the External Surface
Micrography close to the external surface of a new tube, sound.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
Micrography of a transverse section of the seam weld, close to the external surface, presenting several cracks perpendicular to the thickness.
24
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the External Surface
Micrography of the transverse section of the NEW TUBE, close to the external surface, showing the austenitic structure with primary carbides network.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface

More from these cases

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
The fracture surface of the casting cylinder presented, close to the external surface, a more ductile aspect of the fracture.
58
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Close to the External Surface
Micrography of the longitudinal section of the cylinder, at the external diameter (right side of the figure), presenting smaller interdendritic graphite flakes in a ferritic-perlitic matrix.
37
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of the painted external surface of the cast cylinder.
25
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polishedDf - Close to the External Surface
Micrographic detail of the painted external surface of the cast cylinder.
26
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the External Surface
Micrographic aspect of the cast cylinder section at the fracture position (top of the figure), close to the external surface (left side). It is possible to see a change in the graphite morphology and matrix.
27
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00112 — 1" XXS Pipe Not Qualified For Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a 0.2 mm decarburized layer, fully ferritic.
35
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
ML00111 — 3/4" XXS Pipe Not Qualified for Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
35
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrography of the longitudinal section of the tube, close to the external surface. A scale is evident at the surface as well as a carburizing layer.
83
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Micrography close to the external surface of the tube removed from service, damaged by high temperature oxidation.
25
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Micrographic detail of the seam weld close to the external surface, presenting the needles that are the result of microstructural evolution and cracks filled with oxides.
26
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the External Surface
Micrography of a transverse section of the circumferential butt weld, close to the external surface, presenting a shallow localized corrosion at the margin of the weld.
28
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the External Surface
Micrographic detail of the circumferential butt weld, close to the external surface, presenting a shallow localized corrosion at the margin of the weld.
27
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the External Surface
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects close to the external surface.
49
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Close to the External Surface
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE,close to the external surface, showing the austenitic structure with coalesced carbides and secondary precipitation.
40
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface