Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Engine Capture method: Nital Etched Micrography by OM clear all

A — sub-branches

126 1532 1536 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the crankshaft at the surface, in the radio that is not heat treated. The microstructure is nodules of graphite in a ferritic and pearlitic matrix, predominantly pearlitic.
96
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the longitudinal section of the cylinder, at the internal diameter (left side of the figure), in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix.
50
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface

More from these cases

ML00154 — High Strength Cast Iron CrankshaftM - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Micrography of the crankshaft close to the radio that is not heat treated. Graphite in nodules and a ferritic and pearlitic matrix, predominantly pearlitic.
81
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Matrix of ferrite and pearlite
Micrographic detail of the graphite nodules and a ferritic and pearlitic matrix, predominantly pearlitic.
82
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Matrix of ferrite and pearlite
Micrography of the shaft at the surface, in a heat treated position. Graphite in nodules. Dark blue martensitic microstructure around the nodules and white islands of martensitic with retained austenite microstructure (not clearly identified at this low magnification).
68
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the shaft very close to the surface, in a heat treated position. Graphite in nodules. Dark blue martensitic microstructure around the nodules, brown yellow martensite and white islands of martensitic with retained austenite microstructure.
65
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the graphite in nodules, dark blue martensitic microstructure around the nodules, brown yellow martensite and white yellow islands of martensitic with retained austenite microstructure.
61
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Martensite

+9 more from this case →

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Micrography of the longitudinal section of the cylinder, at the internal diameter, in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix. It is important to mention that the flakes are almost interconnecting themelves.
47
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Graphite in Flakes
Micrography of the longitudinal section of the cylinder, at the internal diameter, in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix. It is important to mention that the flakes are almost interconnecting themelves.
48
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Predominantly Pearlitic
Micrography of the longitudinal section of the cylinder, in the center of the thickness, presenting large graphite flakes in a predominatly perlitic matrix.
49
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the longitudinal section of the cylinder, in the center of the thickness, presenting large graphite flakes in a predominatly perlitic matrix. There are also ferritic regions.
33
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Graphite in Flakes
Micrography of the longitudinal section of the cylinder, in the center of the thickness, presenting large graphite flakes in a predominatly pearlitic matrix.
31
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Predominantly Pearlitic

+12 more from this case →