API

4 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Capture method: Optical Microscope Detail focus: Damage clear all

API — sub-branches

5CT 25D 15L 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the pipe in the leakage area, showing the preferential corrosion in the center of the autogenous weld and oxides inside the crevice, that appearas as a cracking but that is only a localized anodic process.
66
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Localized Corrosion
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
The micrography in the as polished condition of the longitudinal section of the pipe close to the washout, shows that at the tool mark tip (notch from the external surface) a fatigue crack already started from a corroded region (pitting).
187
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Pitting
The micrography shows the region underbead, of the tube HAZ, responsible for the hydrogen cracking (fracture in the right side of the photo - black). The hardness of the HAZ is about 600 HV.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking

More from these cases

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Micrographic detail of the autogenous seam weld. The localized dissolution occurrs exactly at the weld metal that presents a bainitic structure of average hardness about 230HV, compared to the heat affected zone presenting average of 202 HV and the base metal presenting average of 180HV.
57
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Localized Corrosion
Micrographic detail presenting the slighltly decarburized ferritic structure, with inclusions, in the center of the weld, surrounded by a bainitic structure and the preferential corrosion in the weld.
51
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Localized Corrosion
Micrography of the pipe in the leakage area, at the internal pipe surface, showing the preferential corrosion in the center of the autogenous weld and oxides inside the crevice. The morphology of the corrosion is similar to a cracking but the analysis show that it is a localized anodic process.
45
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Preferential Dissolution
Micrography of the pipe at the leakage position showing an oxide layer inside the crevice. The corrosion occurred exactly at the weld metal and the region at the margin of the damage shows the heat affected zone of the autogenous weld, with a refined grain size.
41
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Preferential Dissolution
Micrography of the internal pipe surface at the leakage position showing an oxide layer inside the crevice. The corrosion occurred exactly at the weld metal and the region at the margin of the damage shows the heat affected zone of the autogenous weld, with a refined grain size.
40
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Preferential Dissolution

+1 more from this case →

ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
48
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
43
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
ML00068 — Corrosion Fatigue of a 5" Drill PipeM - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail, in the as polished condition, of the corrosion fatigue crack.
90
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fatigue Crack
The micrography of one of the (multiple) cracks shows the slightly irregular morphology of the cracking, typical of a corrosion-fatigue mechanism.
281
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
Micrographic detail of the slightly irregular crack propagation, typical of a corrosion-fatigue mechanism.
76
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking