ALLOY

3 cases · 17 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Granular Capture method: Naked Eye or Stereoscope clear all

ALLOY — sub-branches

5083 1625 1AA 6061 T6 1P550 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
61
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
The macrography of a longitudinal section shows the low alloy (C-Mn) steel pipe, internally cladded with Ni alloy clad plate.
72
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Longitudinal Section
Macrography of the flat position welded joint. It was welded in three passes, with the following parameters. Root pass - 157A, 21V, 146mm/s (wire speed), 3.2 mm/s (welding speed), 1090 J/mm. Second pass - 161A, 21V, 146mm/s (wire speed), 4.2 mm/s (welding speed), 833 J/mm. Third pass - 155A, 21V, 146mm/s (wire speed), 5.1 mm/s (welding speed), 664 J/mm.
48
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Flat Position

More from these cases

ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Detail of the position where the projectile strike the plate. The plate suffered a localized perforation.
29
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Low Mag
Detail of the position where the projectile exited the plate. The plate suffered a localized perforation.
32
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Low Mag
Detail of the margin of the perforated hole in the impact position. It is interesting to observe that the perforation caused the material to be expulsed from the hole, in the direction of the impact.
31
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Plastic Deformation
Aspect of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
23
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Macrography of the 3/8" thickness aluminum alloy plate, in a section. The side of bullet impact is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet (to the bottom of the figure).
19
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched MacroDf - Transverse Section

+2 more from this case →

ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Macrographic detail of the flat position welded joint, showing the three passes. The large extension of the heat affected zone in the root reveals the too high imposed energy, melting out of the root gap. The shining spots are pores.
42
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Flat Position
Macrography of the horizontal position joint. It was welded in three passes, and one additional pass from the root. Root pass - 153A, 20V, 156mm/s (wire speed), 3.5 mm/s (welding speed), 933 J/mm. Second pass - 162A, 20V, 156mm/s (wire speed), 5.8 mm/s (welding speed), 592 J/mm. Third pass - 155A, 19V, 156mm/s (wire speed), 5.9 mm/s (welding speed), 523 J/mm. Additional at the root - 161A, 23V, 187mm/s (wire speed), 8.5mm/s (welding speed), 467J/mm.
47
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Horizontal Position
Macrographic detail of the horizontal position welded joint, showing the three passes welded from one side and the fourth pass welded after removing the ceramic backing. Big pores and liquation were identified.
40
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Horizontal Position
Macrography of the vertical up position welded joint. It was welded in three passes, with the following parameters. Root pass - 115A, 21V, 162mm/s (wire speed), 2.6 mm/s (welding speed), 1090 J/mm. Second pass - 143A, 21V, 162mm/s (wire speed), 5.5 mm/s (welding speed), 594 J/mm. Third pass - 144A, 21V, 162mm/s (wire speed), 6.1 mm/s (welding speed), 979 J/mm.
39
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Vertical Up Position
Macrographic detail of the vertical up position welded joint, showing the three passes. The second and third passes penetrated to much, almost through wall thickness. The shining spots are pores, some of a large size.
41
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Vertical Up Position

+2 more from this case →