AISI

2 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Optical Microscope Detail focus: Secondary Cracks clear all

AISI — sub-branches

1020 11045 1304 1310 1316 3347 Nb stabilized 1410 24130 34140 3420 24330V 14340 24820 16150 28620 1D2 1Dual grade 316/316L 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of a stud longitudinal section in the first thread fillet adjacent to the fracture, presenting a large secondary crack without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
47
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
Micrography of the longitudinal section of the bolt, in the center of the thickness, showing at the fracture surface (top of the figure), secondary cracks that are perpendicular to the fracture, associated to segregation bands.
55
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

More from these cases

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Low magnification micrography showing how the large secondary crack propagated in the thickness of the stud, with a branching aspect, different than the propagation close to the bottom of the thread fillet.
47
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
Low magnification micrography of the bottom of the thread fillet, presenting secondary cracks, not yet opened.
44
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
37
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Secondary Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
35
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Secondary Cracks
Micrography of the bottom of the thread fillet, presenting secondary cracks of intergranular morphology, not yet opened.
33
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+1 more from this case →

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the longitudinal section of the bolt, in the center of the thickness, showing the secondary cracks associated to segregation bands.
63
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks