Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Segregation Bands clear all

A — sub-branches

193 1691 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
Aspect of the broken stud that was fastening a flanged line in a subsea body (tapped hole) using a nut. The fracture, transverse to the stud axis, occurred exactly at the body to flange interface. Adjacent to the fracture, all thread fillets (positioned inside the flange hole) presented cracks at the bottom of the thread. The stud was operating during seven years and was not corroded, indicating it was protected by the anodes. There are also deposits in the fillets suggesting the cathodic protection was effective even inside the flange hole.
799
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL SURFACE - The micrography (transverse to the tube) presents the ferritic/pearlitic/bainitic structure.
75
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Granular structure
BASE METAL SURFACE - The microstructure of the base metal is ferritic/pearlitic/bainitic.
74
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Grain refined structure
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ

+20 more from this case →

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Longitudinal section micrography in a position of the thread, far from the failure. The stud presented a quenching and tempering structure and the thread was machined.
84
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Microstructure of the stud in the longitudinal section, presenting segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration.
69
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Microstructure of the stud in the longitudinal section, out of a region of segregation, where the tempered martensitic microstructure appears more uniform.
72
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration. The localized microhardness (50g) in the band showed levels about 540HV, and out of the band, in the same localtion, presented an average hardness of 321 HV, indicating that the material is non uniform in the regions where there are bands.
66
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrographic detail of the martensitic structure of the stud in the longitudinal section, out of a region of segregation, where the microstructure appears more uniform and the microhardness is about 370HV (50g).
62
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite

+24 more from this case →