Welded Joint

2 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Testpiece aspect clear all

Welded Joint — sub-branches

Cladding 4Fabrication Weld 15In Field Weld 3Remanufacture by Welding 1Repair Weld 2Welded Testpiece for Qualification 4

Results

SortNewestOldestTitle A-ZTitle Z-A
The small sample removed for analysis. This wedge sample presents three faces: one polished face (that corresponds to the surface), one fractured face and one cut face.
38
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Testpiece aspectDf - Fracture
Tensile testpieces after testing. The rupture of the testpieces occurred at the margin of the weld.
39
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Testpiece aspectDf - Flat Position

More from these cases

ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Tensile testpieces after testing. The rupture of the testpieces occurred at the margin of the weld.
35
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Testpiece aspectDf - Horizontal Position
Tensile testpieces after testing. The rupture of the testpieces occurred at the margin of the weld.
36
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Testpiece aspectDf - Vertical Up Position
Tensile testpieces after testing. The rupture of the testpieces occurred at the margin of the weld.
39
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Testpiece aspectDf - Overhead Position
Broken bending testpiece of the 3G position. The presence of cracks at the root caused the lack of material ductility and opening of cracks during bending. The procedure was not qualified.
46
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Testpiece aspectDf - Cracks