Welded Joint

3 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Refined ferritic Capture method: Optical Microscope Detail focus: Microstructure clear all

Welded Joint — sub-branches

Fabrication Weld 2Welded Testpiece for Qualification 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the very refined ferritic structure of the base metal, in the longitudinal section, indicating that the material was heat treated, since no banding is not detectable at this magnification.
101
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Grain refined structure
Micrographic detail of the AISI 4130 forging, 5/8" thickness, close to the welded region, in the longitudinal section. Bainitic and tempered martensitic structure.
47
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the weld metal in a cracked region. Non tempered martensitic regions. This part is not typically stress relieved after welding.
50
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite

More from these cases

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrographic detail of the bainitic structure of the coarse grain heat affected zone, close to the fusion line (to the top of the figure).
76
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Bainitic HAZ
Micrographic detail of the weld metal in the last bead. The microstructure shows primary ferrite in the (previous austenite) grain boundaries, some regions of ferrite with aligned second phases and acicular ferrite in the center of the columnar grains.
51
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Columnar Grains
Micrographic detail of the refined ferritic microstructure, with equiaxial grains, of the weld metal in the root, reheated by the fill pass. At this magnification it is possible to see that the agglomerated carbides ar located in ferritic grain boundaries.
67
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Equiaxial Grains
ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Micrographic detail of the X65 pipe, 5/8" thickness, in the longitudinal section. The refined ferritic structure with bainitic bands is responsible for obtaining the 65 Ksi YS for a low carbon manganese ferritic structure.
48
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Banded Structure