Welded Joint

18 cases · 31 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Aspect Before Analysis clear all

Welded Joint — sub-branches

Cladding 4Fabrication Weld 15In Field Weld 3Remanufacture by Welding 1Repair Weld 2Welded Testpiece for Qualification 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the hydraulic line samples removed from service to be analyzed. Tubing and welded joint (bottom sample) between the 316 tubing (left side of the sample) and the nitronic fitting (right side of the sample). The cracking is located 10 mm far from the weld, autogenous orbital GTAW.
108
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
Aspect of the fitting welded to a tubing, ND 5/8" in a hydraulic line. The through wall cracking is longitudinal in the fitting side.
1032
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
Fracture occurred during fabrication of a low carbon steel automotive part, welded by SAW process in one fillet, between a superior plate (8mm thick) and an inferior plate (12 mm thick). See the schematic drawing in the next figure.
290
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Fracture
The connector was welded to the pipe from both (internal and external) sides, a PWHT was applied and the part was machined. The UT indication was detected during final inspection.
78
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Aspect of the fillet weld between the superior plate (Low carbon 8 mm thick) and the inferior plate (C-Mn 12 mm thick), in an overlap geometry. In this region the welded joint was sound.
90
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Welded Joint
The 8" ND, 1 1/4" thick, seamless pipe that was welded by GMAW process in 6G position. The testpiece was adopted for ASME IX qualification tests.
402
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The 2 1/2" nominal diameter seamless tube is externally cladded with stainless steel.
196
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Aspect Before AnalysisDf - Welded Joint
Steam drum presenting cracks in the shell, connecting tube holes.
1704
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Cracking

More from these cases

ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Detail of the welded joint between the 316 tubing (left side) and the nitronic fitting (right side). The through wall cracking is transverse to the line, in the fitting, 10 mm far from the weld, where the fitting was slightly bent to be assembled (cold bent).
65
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Welded Joint
ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Detail of the longitudinal through wall cracking in the fitting welded to a tubing, ND 5/8" in a hydraulic line.
87
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the internal side of the fitting to tubing welded joint, after longitudinal cut. It is possible to see that the cracking (still filled with corrosion products) is located in the fitting side (left side) far from the welded joint to the tubing (right side).
58
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Internal Surface
ML00067 — Cold Cracks in C-Mn SAW Weld MetalM - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Aspect of the fracture in the middle of the fillet weld between the superior plate (Low carbon 8 mm thick no longer there) and the inferior plate (C-Mn 12 mm thick), in an overlap geometry.
77
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Fracture