Aspect of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
23
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the titanium alloy, in a section transverse to the impact position that is to the top of the figure. The projectile did not perforate the plate but caused a localized plastic deformation and cracks that appear in the opposite site of the plate at the projectile impact position.
11
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
53
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the AR500 wear resistant steel, in a section transverse to the impact position evidencing lack of plastic deformation, or any other damage. The impact surface is to the top of the figure.
28
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
The macrography of a longitudinal section of the shell plate (sample removed from the boiler), at the position of the fillet weld (sealing weld) with a tube, where surface welding repairs created conditions for cracking the base material in a transgranular morphology. Several cracks were identify starting from the steam drum internal surface.
448
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Transverse Section AspectDf - Cracks

More from these cases

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the titanium alloy, in a section transverse to the impact position that is to the top of the figure. The projectile did not perforate the plate but caused a localized plastic deformation and a shear effect.
15
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
Macrography of the 3/8" thickness titanium alloy plate, in a section. The side of bullet impact is to the top of the figure. The impact sheared the plate wall in a very localized position. HF+HNO3+H2O chemical etch.
20
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Plastic Deformation
Macrography of the 3/8" thickness titanium alloy plate, in a section. The impact side of the plate is to the top of the figure. The plate was sheared through wall in a very localized position. HF+HNO3+H2O chemical etch.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Ductile Crack
Macrography of the 3/8" thickness titanium alloy plate, in a section. The side of bullet impact is to the top of the figure. The impact sheared the plate wall in a very localized position. HF+HNO3+H2O chemical etch.
12
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Ductile Crack