Raw Material

4 cases · 40 images for “embrittlement”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Optical Microscope clear all

Raw Material — sub-branches

Carburized 1Casting 1Chromium Plated 1Forging 1Rod 1Wire 1

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Micrography of the high strenght steel, heat treated, of the casting device. The microstructure is bainitic martensitic.
109
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainitic Martensitic
Micrography of a longitudinal section of the pin, in the center. The low carbon content of the steel in the center of the pin makes the structure bainitic even though it was quenched and tempered after carburizing.
80
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the longitudinal section of the forging material, presenting a granular austenite, precipitation hardened.
84
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
The longitudinal section of the spring wire shows a strain hardened martensitic structure, aged to high strength (602 HV 0.3kg). Previous austenite grains are elongated.
55
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrography of the high strenght steel, heat treated, of the casting device. The microstructure is bainitic martensitic.
92
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainitic Martensitic
Micrographic detail of the high strenght steel microstructure, bainitic martensitic.
85
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainitic Martensitic
Micrographic detail of the zinc layer at the surface.
88
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Zn Layer
Micrography of the section transverse to the fracture (top of the figure). The fracture is intergranular, there are several secondary cracks, and there are deposits of zinc over the fracture. The zinc makes difficult the etch with Nital to reveal the microstructure close to the fracture surface.
67
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture
Micrographic detail of the section transverse to the fracture (top of the figure), suggesting the intergranular morphology (at the previous austenite grain boundaries) and the deposits of zinc over the fracture that create a condition of protection of the base metal during the metallographic etch, and the material is not fully etched.
60
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Zn Layer

+12 more from this case →

ML00081 — Hydrogen Cracking of a Chromium Plated Carburized PinM - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Micrographic detail of the bainitic structure in the center of the pin, that was quenched and tempered after carburizing.
75
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pin, at the surface. The pin was carburized, quenched and tempered (yellow diffuse layer at the surface, 0.5 mm of extension) and a white layer of hard chromium plating is evident.
108
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Carburized Layer
Micrographic detail a longitudinal section of the pin, at the surface, showing the case hardened. The pin carburized, quenched and tempered structure presents a gradient of carbon content and consequently a gradient of martensitic structure and hardness. Close to the surface the hardness level is 742 HV1 .
87
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic detail of the high hardness martensitic structure at the surface of the pin, that was quenched and tempered after carburizing.
67
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography that presents a secondary cracking (adjacent to the broken surface) propagating 500 microns from the surface, where there is a white layer of hard chromium .
78
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Carburized Layer

+3 more from this case →

ML00078 — Hydrogen Cracking of IN 718 Subsea ConnectorM - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the conector, at the fracture position, showing secondary cracks from the fracture surface.
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
The micrographic detail of the longitudinal section at the fracture surface shows intergranular morphology for the secondary cracks (longitudinal to the forging axis).
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks.
54
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
48
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the strain hardened aged martensitic structure. Small aligned delta ferrite islands can be seen.
51
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
The transverse section of the spring wire shows a strain hardened martensitic structure, aged to high strength (602 HV 0.3kg).
48
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Transverse Section
Micrographic detail of the strain hardened aged martensitic structure.
48
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Transverse Section
Micrography of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism.
37
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OM using A262 Method ADf - Secondary Cracks
Micrographic detail of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism. The electrolytic oxalic acid etch reveals the delta ferrite phase. Compare with the Kalling etch in the other figure.
31
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OM using A262 Method ADf - Fracture

+2 more from this case →