Raw Material

3 cases · 40 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Mechanical Industry clear all

Raw Material — sub-branches

Casting 1Forging 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the fracture surface of the 2" diameter casting. The fracture appeared flat, with secondary cracks, and the position of the fracture during the loading test is located in the region that was in tensile stress during the hot dip galvanized process (the part was sustaining its own weight during the zinc hot dip bath).
801
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Aspect of the serrated walrus tool, interchangeable, that was removed at the end of its life. Dimensions of 1" thick, 2" width, 3" long.
419
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
The shaft presented a light wear at the end of the life. See the schematic drawing in the next figure
597
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrography of the high strenght steel, heat treated, of the casting device. The microstructure is bainitic martensitic.
109
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainitic Martensitic
Micrography of the high strenght steel, heat treated, of the casting device. The microstructure is bainitic martensitic.
92
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainitic Martensitic
Micrographic detail of the high strenght steel microstructure, bainitic martensitic.
85
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Bainitic Martensitic
Micrography of the casting at the surface, presenting a zinc layer deposited in a hot dip process. The thickness of the layer is about 0.3mm in this position, that is higher than expected for this process. The steel substrate is not revealed because the etch was light and the zinc layer protects the low aloy steel during the etch.
93
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by SEMDf - Zn Layer
Micrographic detail of the zinc layer at the surface.
88
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Zn Layer

+24 more from this case →

ML00084 — Walrus Tool SteelM - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Micrography of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite. The tempering was in low temperature since the hardness is high (58 HRc at the surface).
87
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Micrographic detail of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite, with small secondary carbides. The hardness in the section is 59 HRc.
73
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Martensite
ML00064 — SAE 1045 Steel ShaftM - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Schematic drawing presenting the Shaft
169
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Identification drawingDf - At the Surface
Micrography of the longitudinal section of the shaft, in the center of the thickness, presenting a ferritic-perlitic structure typical of a hot forming process.
149
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of the ferritic-perlitic structure, typical of a hot forming process, in the center of the thickness.
139
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of the ferritic-perlitic structure, typical of a hot forming process, in the center of the thickness.
116
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the longitudinal section of the shaft, at the damaged surface (with a light wear). In low magnification the ferritic perlitic texture reveals the forging lines.
102
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface

+1 more from this case →