Pipe

2 cases · 27 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: S31603 clear all

Pipe — sub-branches

Seamless Pipe 2

Results

SortNewestOldestTitle A-ZTitle Z-A
General view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity. The branch line is composed by a seamless pipe welded to a weldolet (left side of the figure) and to a flange (right side of the figure). The leakage is associated to a through wall cracking in the middle of the pipe length. The cracking is not evidenced in the figure, since it is too thin. See the schematic drawing in the next figure
494
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Transverse section of the 2" diameter pipe at the pitting location. The pipe was leaking.
1322
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Transverse Section AspectDf - Pitting

More from these cases

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Schematic drawing presenting the general view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity.
94
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Identification drawingDf - General View
Aspect of the internal surface of the pipe after longitudinal cutting, presenting a straight cracking, circumferential. The weldolet is to the left side and the flange is to the right side. See the schematic drawing in the next figure.
89
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Schematic drawing presenting the cracking surface aspect.
71
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Identification drawingDf - Internal Surface
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking

+13 more from this case →

ML00014 — Pitting Corrosion in 316SS PipeM - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
The external surface of the 2" diameter pipe is rusted and the leakage is associated to “holes” that appear very small at the surface but that open a large hole in the middle of the thickness.
507
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Corrosion
Image of the external surface of the pipe presenting regions of localized corrosion (in the beginning) and deposits
387
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion
Image of the external surface of the pipe presenting deposits where there is a localized corrosion at the surface.
326
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion
Image of the external surface of the pipe presenting the aspect of the localized corrosion by pitting.
297
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Pitting
Micrography of a transverse section of the pipe, presenting the pitting corrosion. As polished.
310
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OMDf - Pitting

+2 more from this case →