Forging

4 cases · 27 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the thread at the valve body surface, showing localized dissolution of the thread.
73
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corroded Thread
Micrography of the longitudinal section of the forging material, presenting a granular austenite, precipitation hardened.
84
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
Longitudinal section of the fitting in the center of the thickness (2"). Refined ferritic structure.
370
VIEW
ML00030 / Jan.2017
Forging for High Pressure Application
M - Microalloyed SteelP - Machined PartAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Bainitic Ferrite

More from these cases

ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Micrography of the valve body carbon steel thread, in the valley. Ferritic-bainitic structure.
77
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Transverse Section
Micrographic detail of the valve body carbon steel thread, in the valley. Ferritic-bainitic structure.
69
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Bainitic Ferrite
Micrography of the valve body carbon steel thread, in the peak. Ferritic-bainitic structure.
64
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corroded Thread
Micrographic detail of the valve body carbon steel thread, in the peak. Ferritic-bainitic structure.
55
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corroded Thread
Cross-section near a threaded surface showing an acicular matrix structure bordered by a dark, layered corrosion/oxide band along the thread root.
1
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Oxide Layer
ML00078 — Hydrogen Cracking of IN 718 Subsea ConnectorM - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the conector, at the fracture position, showing secondary cracks from the fracture surface.
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
The micrographic detail of the longitudinal section at the fracture surface shows intergranular morphology for the secondary cracks (longitudinal to the forging axis).
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks.
54
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
48
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
The liquation crack is a hot crack in the base metal (at the HAZ) that induces a solidification crack in the weld metal.
66
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrographic detail of the cracks at the fusion line of the welded joint, at the connector side. The cracking presents morphology of melting regions of impurities at grain boundaries of the large grains of the heat affected zone (HAZ).
57
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
48
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
43
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
Micrography of the AISI 4130 forging, 5/8" thickness, close to the welded region, in the longitudinal section.
42
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal Left Side

+7 more from this case →

ML00030 — Forging for High Pressure ApplicationM - Microalloyed SteelP - Machined PartAp - Oil and GasCd - Typical manufacturing
Longitudinal section of the fitting in the center of the thickness (2"). Refined ferritic structure.
67
VIEW
ML00030 / Jan.2017
Forging for High Pressure Application
M - Microalloyed SteelP - Machined PartAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Grain refined structure
Longitudinal section of the fitting in the center of the thickness (2"). Refined ferritic structure.
63
VIEW
ML00030 / Jan.2017
Forging for High Pressure Application
M - Microalloyed SteelP - Machined PartAp - Oil and GasCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Grain refined structure