Casting

3 cases · 43 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Sound clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
As received aspect of the sacrificial casting, 2" internal diameter. The casting was solution annealed heat treated.
488
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
General view of the nodular cast iron crankshaft, 240 mm long, in process of heat treatment. The main and rod bearings, 54 mm diameter, are heat treated by localized quenching and tempering.
1018
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Aspect Before AnalysisDf - General View
Grey cast iron microstructe. Perlitic matrix and graphite flakes.
507
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Pearlite Matrix

More from these cases

ML00164 — Austenitic SS Casting for Valve BodyM - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Macrography of a longitudinal section of the valve body, presenting the granular structure. The main bore diameter is 2". The casting was tested in two positions. In radial direction in the center of the body (3" solid), and in the longitudinal direction in the wall (1" thick).
78
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Longitudinal Section
Micrography of a longitudinal section, in the center of the valve body, solid 3" thickness. The structure is austenitic with delta ferrite in interdendritic spaces.
67
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrography of a longitudinal section, in the center of the valve body. The structure is austenitic with delta ferrite in interdendritic spaces. The austenite presents a cored matrix in the dendrites, indicating the chemical composition was not homogeneized during the heat treatment.
60
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Oxalic Acid Electrolytic EtchDf - Delta ferrite
Micrographic detail of the cored austenitic structure with delta ferrite in interdendritic spaces. The chemical composition was not homogeneized during the heat treatment.
55
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Oxalic Acid Electrolytic EtchDf - Delta ferrite
Micrography of a longitudinal section, in the 1" thickness valve wall. The structure is austenitic with delta ferrite in interdendritic spaces.
48
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Oxalic Acid Electrolytic EtchDf - Austenite

+2 more from this case →

ML00154 — High Strength Cast Iron CrankshaftM - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Micrography of a crankshaft longitudinal section at the shaft edge, in the as polished condition, presenting nodular graphite, well distruibuted.
139
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - At the Surface
As polished micrography of the crankshaft at the shaft edge, close to the surface. Graphite in nodules.
126
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - Graphite in Nodules
As polished micrographic detail of the graphite in nodules, close to the surface of the shaft edge, in a longitudinal section.
114
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - Graphite in Nodules
Macrography of a longitudinal section of the crankshaft showing the rod bearing in the center (the rod is 54mm diameter), as well as two main bearings in both lateral sides. It is possible to see that the surface was heat treated and the hardened layer is about 3mm deep from the surface.
100
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - NItal Etched MacroDf - Longitudinal Section
Macrographic detail of the hardened layer, about 3mm deep from the surface. Important to observe that the bearing is not heat treated in the radius, only in the contact area. The hardness at the surface is 430HV and the hardness in the base metal is 260HV.
100
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - NItal Etched MacroDf - Surface Layer

+22 more from this case →

ML00032 — Cast Iron Case of Drilling EquipmentM - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Low magnification micrography presenting the grapjite morphology.
138
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Micrography by OMDf - Graphite Type A (ASTM A247)
Grey cast iron structure. As polished.
109
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Micrography by OMDf - Graphite in Flakes
Grey cast iron with graphite in flakes.
97
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Micrography by OMDf - Graphite in Flakes
Grey cast iron with graphite in flakes and perlitic matrix.
110
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Perlite Matrix
Grey cast iron microstructe. Perlitic matrix and graphite flakes.
85
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite Type A (ASTM A247)

+1 more from this case →