Casting

3 cases · 19 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Energy Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
419
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Original casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
50
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Micrographic detail of the defect (void in the right side of the figure), as polished. In the left side it is the surface of the water blade and there are some non metalic inclusions in this region.
54
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Micrography by OMDf - Void

More from these cases

ML00058 — High-Pressure Piston Seal in Casting Al AlloyM - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
45
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
34
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
32
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Inserted casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Micrography of the original casting blade at the fusion line of the welding with the insert casting. There is a refinement effect on the coarse base metal structure.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Left Side
Micrographic detail of the fusion line of the original casting blade welded to the insert casting. There is a refinement effect on the coarse base metal structure.
21
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Left Side
Micrography of the inserted casting at the heat affected zone of the welding with the original casting. There is a refinement effect on the coarse base metal structure.
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Right Side
Micrographic detail of the fusion line of the inserted casting welded to the original casting. There is a refinement effect on the coarse base metal structure.
15
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Right Side

+2 more from this case →

ML00017 — Casting Defect in CA6NMM - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Micrographic detail non metalic inclusions in the region where there are casting defects. As polished.
48
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Micrography by OMDf - Non Metallic Inclusions
Blade microstructure. Tempered martensite, (probably) retained austenite and delta ferrite islands.
55
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Kalling Etched Micrography by OMDf - Delta Ferrite Islands
Blade microstructure. Previous austenite coarse grains.
46
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Kalling Etched Micrography by OMDf - Coarse Structure
Blade microstructure. Tempered martensite, (probably) retained austenite and delta ferrite islands.
47
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Kalling Etched Micrography by OMDf - Delta Ferrite Islands
Region of a casting void in the blade.
33
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Kalling Etched Micrography by OMDf - Void

+1 more from this case →