Bolt

2 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Kalling Etched Macro clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The macrography shows the longitudinal section of the allen bolt, 1/2" nominal diameter, that was machined from a heat treated bar (solution annealed and aged). The granular structure presents differences in the grain sizes. At the bolt head (external surface of the original bar) the austenitic grain size is larger than in the center of the bar where the particles in segregated bands "arrested" the grains during hot forming and solution annealing.
58
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched MacroDf - Machined Thread
Macrography of a longitudinal section of the broken bolt, at the fracture position, showing that the fracture is partially flat (left side), where the macroscopically aspect is brittle, and a final ductile fracture (right side). Interesting to note that there is a large longitudinal crack, secondary (transverse to the fracture surface).
143
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Longitudinal Section

More from these cases

ML00089 — Inconel 718 Allen Bolt for Subsea ApplicationM - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Micrographic detail of a longitudinal section of the bolt, in the center of the thickness (ND 1/2"). Although the material was hardened by heat treatment (solution annealing and aging), the microstructure observed by optical microscopy does not reveal the intragranular precipitation.
33
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched MacroDf - Austenite
The micrography of a longitudinal section, at the bolt head close to the surface of the original bar. In this region the material increased the grain size due to the lack of particles (inclusions), to "arrest" the grain boundaries (during hot forming and solution annealing). The smaller grain size is located in the center of the bar, that concentrated the inclusions.
30
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched MacroDf - Dual grain sizes