Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Condition: Damage Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the longitudinal section, in the center of the thickness of the pin, presenting an aligned ferritic-austeinitic structure.
180
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
As polished micrographic aspect of the longitudinal section of the cylinder, at the surface, in a region where the damage is in the begining. It is possible to see that there are two layers at the surface. A first Ni layer, 300HV average hardness, over the low carbon steel substrate, 200HV average hardness, and a chromium plated layer, 1100HV average hardness and several discontinuities.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Longitudinal Section

More from these cases

ML00146 — Plastic Deformation of a SDSS Riser PinM - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Micrography of a longitudinal section, at the surface of the pin, where the thermal spray layer is sound. The thickness of the layer is about 0.3 mm.
168
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Coating Layer
Micrographic detail of a longitudinal section of the pin, at the surface, evidencing the thermal spray layer, about 0.3 mm. The layer presents typical characteristics of multiple layers, low amount of entrapped oxides and pores. The interface presents a high roughness level for a good adherence and some entrapped oxides. The structure of the SDSS substrate did not show thermal effects.
154
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Coating Layer
Micrography of a longitudinal section, at the damage surface of the pin, where the thermal spray layer was partially detached and broken. The through layer breaking is ductile, typical of an overloading condition caused by the localized bending of the pin.
109
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
Micrographic detail of the damage surface layer, detached and broken. The substrate is not affected and the rupture of the layer is typically by overloading.
117
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
ML00128 — MIC of a Stored Hydraulic CylinderM - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Micrographic aspect of the Cr layer at the surface presenting incipient damage. Microcracks of the Cr layer, associated to small pits.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Cracks
Micrographic aspect, after Nital etching, of the longitudinal section of the cylinder, at the surface, in a region where the damage is in the begining. There are two layers at the surface. A first Ni layer, 160 microns thick and 300HV average hardness, over the low carbon steel substrate, 200HV average hardness, and a chromium plated layer, 250 microns thick and 1100HV average hardness.
59
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corrosion
Micrographic detail of the longitudinal section of the cylinder, at the surface, in a region where the Cr layer is detaching.
56
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corrosion
Micrographic aspect of the longitudinal section of the cylinder steel substrate, presenting a ferritic-pearlitic structure.
207
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic structure of the cylinder steel substrate.
41
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+3 more from this case →