Titanium Alloy

4 cases · 28 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: ASTM Capture method: Optical Microscope clear all

Titanium Alloy — sub-branches

Ti6Al4V 2Unalloyed Titanium 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography transverse to the fillet weld in the pipe. The pipe base metal is to the bottom of the figure and the weld metal is to the top. The heat affected zone in the middle, shows a coarse grain size structure.
59
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Welded Joint
The microstructure of the pipe base metal, in the center of the thickness, is granular alpha.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Granular structure
The plate longitudinal section presents a granular refined structure. Biphasic.
340
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Grain refined structure
The bar presented a large prior beta grain size and acicular alpha. Biphasic structure.
420
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Coarse Structure

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Low magnification micrography showing the weld metal, full of pores, indicating that the field welding was not properly shileded.
50
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Granular alpha structure of the pipe base metal.
49
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Alpha
Coarse grains in the heat affected zone.
46
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Heat Affected Zone
Micrography of the weld metal at the fillet weld where the cracking started, showing several brittle microcracks that corresponds to the regions where the fractography showed secondary crackis.
35
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal brittle microcracks, in regions with hydrides formation.
32
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal

+10 more from this case →

ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
The pipe base metal, at the internal surface, presents a hydride layer showing that the environment is absorbing hydrogen. Although there are microcracks in this layer it did not detach in the base metal.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Hydride Formation
The microstructure of the pipe seam weld metal, in the center of the thickness, presents a coarse prior beta grain size.
85
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Columnar Grains
The pipe internal suface, at the welded region, presents no hydride layer (because it has detached) as well as the material itself is suffering brittle detachment.
71
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning
Detail, as polished, of brittle cracks in the weld metal, from the internal side of the pipe.
67
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by OMDf - Brittle Cracks
Seam weld of the pipe showing the localized thinning in the weld metal, caused by the detachment of the hydride layer and brittle behaviour of the coarse weld metal structure.
64
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning
ML00029 — Titanium Plate for Subsea ApplicationM - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Alpha and beta phases. Refined Structure.
52
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
Alpha and beta phases. Refined Structure.
46
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
ML00028 — Titanium Bar for Subsea ApplicationM - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
The bar presented alpha plus beta phases, acicular alpha and coarse prior beta grains.
97
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
Acicular alpha structure in a biphasic alloy of a large prior beta grain size. 4" diameter bar.
100
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Acicular Alpha