Titanium Alloy

2 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Condition: Damage Capture method: Optical Microscope clear all

Titanium Alloy — sub-branches

Ti6Al4V 1Unalloyed Titanium 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the plate in the middle of the thickness, showing the aligned structure tyical of a rolling process. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
The microstructure of the pipe base metal, in the center of the thickness, is granular alpha.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Granular structure

More from these cases

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography showing the alpha plus beta microstructure in the middle of the thickness. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
32
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the alpha (light grains as a matrix) plus beta (dark phase) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta phase (dark) in the alpha grains (light) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
24
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta (dark phase) in alpha microstructure. Etched with HF+ HNO3+H2O solution.
26
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrography by SEM of the plate in the middle of the thickness, showing the alpha microstructure (dark grains) and the beta phase (light). Etched with HF+HNO3+H2O.
35
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta

+12 more from this case →

ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
The pipe base metal, at the internal surface, presents a hydride layer showing that the environment is absorbing hydrogen. Although there are microcracks in this layer it did not detach in the base metal.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Hydride Formation
The microstructure of the pipe seam weld metal, in the center of the thickness, presents a coarse prior beta grain size.
85
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Columnar Grains
The pipe internal suface, at the welded region, presents no hydride layer (because it has detached) as well as the material itself is suffering brittle detachment.
71
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning
Detail, as polished, of brittle cracks in the weld metal, from the internal side of the pipe.
67
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by OMDf - Brittle Cracks
Seam weld of the pipe showing the localized thinning in the weld metal, caused by the detachment of the hydride layer and brittle behaviour of the coarse weld metal structure.
64
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning