Titanium Alloy

3 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Naked Eye or Stereoscope clear all

Titanium Alloy — sub-branches

Ti6Al4V 1Unalloyed Titanium 3

Results

SortNewestOldestTitle A-ZTitle Z-A
The through wall cracking was opened by longitudinal cutting of the pipe in two positions, to analyzed the region where the crack was nucleated.
33
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Macroscopic aspect of the fracture surface.
37
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
34
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Aspect of the opened crack, showing the flat fracture. The through wall cracking started at the welded region at the end of the rib.
39
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Hydrides in Titanium Weld
4
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The propagation of the crack is also transgranular, without plastic deformation, by fatigue.
26
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fatigue Striation
Aspect of the broken part of the blade that felt and was removed without disassembling the instrument. The fracture is to the top and at the blade surface it is possible to see secondary cracks propagating from the main crack.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Secondary Cracks
ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Detail of the position where the projectile strike the plate. The plate suffered a localized plastic deformation.
18
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface AspectDf - Low Mag
Detail of the position observed form the back side of the plate, where the projectile deformed the plate and cracked it.
19
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface AspectDf - Low Mag
Detailed aspect of the surface of the plate at the projectile impact position.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface AspectDf - Melted film
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the titanium alloy, in a section transverse to the impact position that is to the top of the figure. The projectile did not perforate the plate but caused a localized plastic deformation and cracks that appear in the opposite site of the plate at the projectile impact position.
11
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the titanium alloy, in a section transverse to the impact position that is to the top of the figure. The projectile did not perforate the plate but caused a localized plastic deformation and a shear effect.
15
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section

+3 more from this case →